Creep behavior and microstructural stability of P23/P91 dissimilar welds during creep at 550°C

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25870807%3A_____%2F14%3A%230000379" target="_blank" >RIV/25870807:_____/14:#0000379 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.metal2014.com" target="_blank" >http://www.metal2014.com</a>

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Creep behavior and microstructural stability of P23/P91 dissimilar welds during creep at 550°C

Popis výsledku v původním jazyce

The paper deals with the study on creep behavior and minor phase evolution in two types of heterogeneous weld joints of P23 and P91 steels during long-term creep exposure at 550 °C. The filler material in Weld A corresponded to P91 steel and the filler metal in Weld B was similar to the chemical composition of P23 steel. The creep rupture tests on the cross-weld test pieces of both welds revealed that most failures occurred in the partly decarburized zones of P23 steel or WM23. The carbon redistributionand the minor phase evolution across the sharp P23/P91 interface were calculated using Thermocalc and Dictra computer packages. The experimental study on minor phase evolution using both EDX and SAED in TEM was in a good agreement with the computer simulations, except for M23C6 phase in P23 (WM23) steel. EBSD technique used to study on microstructure changes along the P23/P91 boundary confirmed the slowing down of the recovery/recrystallization processes in the partly decarburized zone

Název v anglickém jazyce

Creep behavior and microstructural stability of P23/P91 dissimilar welds during creep at 550°C

Popis výsledku anglicky

The paper deals with the study on creep behavior and minor phase evolution in two types of heterogeneous weld joints of P23 and P91 steels during long-term creep exposure at 550 °C. The filler material in Weld A corresponded to P91 steel and the filler metal in Weld B was similar to the chemical composition of P23 steel. The creep rupture tests on the cross-weld test pieces of both welds revealed that most failures occurred in the partly decarburized zones of P23 steel or WM23. The carbon redistributionand the minor phase evolution across the sharp P23/P91 interface were calculated using Thermocalc and Dictra computer packages. The experimental study on minor phase evolution using both EDX and SAED in TEM was in a good agreement with the computer simulations, except for M23C6 phase in P23 (WM23) steel. EBSD technique used to study on microstructure changes along the P23/P91 boundary confirmed the slowing down of the recovery/recrystallization processes in the partly decarburized zone

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/LO1203" target="_blank" >LO1203: Regionální materiálově technologické výzkumné centrum - Program udržitelnosti</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

The 23rd Anual International Comference of Metallurgy and Materials METAL 2014

ISBN

978-80-87294-52-9

ISSN

—

e-ISSN

—

Počet stran výsledku

7

Strana od-do

—

Název nakladatele

TANGER spol. s r.o.

Místo vydání

Brno

Místo konání akce

Brno

Datum konání akce

1. 1. 2014

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—