Materialographic Analysis of MAR M-247 Superalloy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25870807%3A_____%2F15%3A%230000422" target="_blank" >RIV/25870807:_____/15:#0000422 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.scientific.net/KEM.647.66" target="_blank" >http://www.scientific.net/KEM.647.66</a>

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Materialographic Analysis of MAR M-247 Superalloy

Popis výsledku v původním jazyce

This paper presents the results of structural phase analysis of MAR-M247 superalloy. Analysis was performed at initial and in as casted state after various type of solution annealing in the range 900 °C to 1240 °C with cooling in water. Presented polycrystalline alloy is heat resisting nickel superalloy, especially usable for highly strained components in the industry producing stationary gas turbines and aircraft engines. Analysis was performed using of a Quanta FEG 450 scanning electron microscope with micro-analytic system Trident APEX-4 which have identified presented minor phase. Attention was also paid to its eventual changes after different type of solution annealing.

Název v anglickém jazyce

Materialographic Analysis of MAR M-247 Superalloy

Popis výsledku anglicky

This paper presents the results of structural phase analysis of MAR-M247 superalloy. Analysis was performed at initial and in as casted state after various type of solution annealing in the range 900 °C to 1240 °C with cooling in water. Presented polycrystalline alloy is heat resisting nickel superalloy, especially usable for highly strained components in the industry producing stationary gas turbines and aircraft engines. Analysis was performed using of a Quanta FEG 450 scanning electron microscope with micro-analytic system Trident APEX-4 which have identified presented minor phase. Attention was also paid to its eventual changes after different type of solution annealing.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/LO1203" target="_blank" >LO1203: Regionální materiálově technologické výzkumné centrum - Program udržitelnosti</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Key engineering materials

ISSN

1013-9826

e-ISSN

—

Svazek periodika

66

Číslo periodika v rámci svazku

647

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

6

Strana od-do

66-71

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—