Creep Resistance and Microstructure Evolution in HR3C-P92 Heterogeneous Welds

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25870807%3A_____%2F23%3AN0000039" target="_blank" >RIV/25870807:_____/23:N0000039 - isvavai.cz</a>

Výsledek na webu

<a href="https://www.scientific.net/DDF.422.51" target="_blank" >https://www.scientific.net/DDF.422.51</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.4028/p-i8lz79" target="_blank" >10.4028/p-i8lz79</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Creep Resistance and Microstructure Evolution in HR3C-P92 Heterogeneous Welds

Popis výsledku v původním jazyce

The paper deals with results of long-term stress rupture tests on „cross-weld“ specimens made of HR3C–P92 heterogeneous welds. Stress rupture tests were carried out in air at temperatures of 625 and 650 °C up to ca 20 000 h to rupture. Creep rupture strength values of HR3C–P92 welds for 104 h at both 625 and 650 °C were calculated. The preferential location of failure was the intercritical part of the heat affected zone in P92 steel. Local changes of hardness during creep exposure were evaluated by hardness profiles across the welds. Metallographic studies were performed in individual parts of heterogeneous welds. A special attention was paid to precipitation reactions in both base materials and heat affected zones.

Název v anglickém jazyce

Creep Resistance and Microstructure Evolution in HR3C-P92 Heterogeneous Welds

Popis výsledku anglicky

The paper deals with results of long-term stress rupture tests on „cross-weld“ specimens made of HR3C–P92 heterogeneous welds. Stress rupture tests were carried out in air at temperatures of 625 and 650 °C up to ca 20 000 h to rupture. Creep rupture strength values of HR3C–P92 welds for 104 h at both 625 and 650 °C were calculated. The preferential location of failure was the intercritical part of the heat affected zone in P92 steel. Local changes of hardness during creep exposure were evaluated by hardness profiles across the welds. Metallographic studies were performed in individual parts of heterogeneous welds. A special attention was paid to precipitation reactions in both base materials and heat affected zones.

Druh

J_SC - Článek v periodiku v databázi SCOPUS

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

<a href="/cs/project/TK03020055" target="_blank" >TK03020055: Výzkum creepového chování a ověřování křehko-lomových vlastností austenitických ocelí pro bloky tepelných elektráren s USC parametry páry.</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2023

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Defect and Diffusion Forum

ISSN

1662-9507

e-ISSN

—

Svazek periodika

422

Číslo periodika v rámci svazku

-

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

6

Strana od-do

51-56

Kód UT WoS článku

—

EID výsledku v databázi Scopus

2-s2.0-85152242338