Metal Dusting Failure in an Aniline Processing Plant

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25870807%3A_____%2F25%3AN0000004" target="_blank" >RIV/25870807:_____/25:N0000004 - isvavai.cz</a>

Výsledek na webu

<a href="http://doi:10.4028/p-uNNa0z" target="_blank" >http://doi:10.4028/p-uNNa0z</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.4028/p-uNNa0z" target="_blank" >10.4028/p-uNNa0z</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Metal Dusting Failure in an Aniline Processing Plant

Popis výsledku v původním jazyce

The paper summarizes the results of the analysis made on the ruptured tube of the reactor made of austenitic stainless steel in which the conversion of aniline to diphenylamine occurs at elevated temperature and pressure and in the presence of a catalyst. The tube wall perforation occurred in the piping used to measure the pressure in the reactor and a fire occurred after an aniline, ammonia and catalyst vapour leak. The material analyses carried out clearly showed that the thinning and subsequent perforation of the tube wall was due to a specific corrosion attack, so-called metal dusting, which occurs at elevated temperatures and in the presence of a carburizing atmosphere.

Název v anglickém jazyce

Metal Dusting Failure in an Aniline Processing Plant

Popis výsledku anglicky

The paper summarizes the results of the analysis made on the ruptured tube of the reactor made of austenitic stainless steel in which the conversion of aniline to diphenylamine occurs at elevated temperature and pressure and in the presence of a catalyst. The tube wall perforation occurred in the piping used to measure the pressure in the reactor and a fire occurred after an aniline, ammonia and catalyst vapour leak. The material analyses carried out clearly showed that the thinning and subsequent perforation of the tube wall was due to a specific corrosion attack, so-called metal dusting, which occurs at elevated temperatures and in the presence of a carburizing atmosphere.

Druh

J_SC - Článek v periodiku v databázi SCOPUS

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2025

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Key Engineering Materials

ISSN

1662-9795

e-ISSN

—

Svazek periodika

1043

Číslo periodika v rámci svazku

27.02.2026

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

7

Strana od-do

91-97

Kód UT WoS článku

—

EID výsledku v databázi Scopus

999