Influence of lithium on the formation and properties of Portland cement clinker

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26232511%3A_____%2F19%3AN0000107" target="_blank" >RIV/26232511:_____/19:N0000107 - isvavai.cz</a>

Výsledek na webu

<a href="https://jcement.ru/magazine/vypusk-6-2019/vliyanie-litiya-na-formirovanie-i-svoystva-klinkera/" target="_blank" >https://jcement.ru/magazine/vypusk-6-2019/vliyanie-litiya-na-formirovanie-i-svoystva-klinkera/</a>

DOI - Digital Object Identifier

—

Jazyk výsledku

ruština

Název v původním jazyce

Влияние лития на формирование и свойства портландцементного клинкера

Popis výsledku v původním jazyce

Потребление лития в производстве батареек и аккумуляторов растет, соответственно будет расти и количество отходов с повышенным содержанием этого металла. Поскольку производство цемента — один из основных потребителей вторичного сырья и промышленных отходов, необходимо изучать влияние лития на свойства клинкера и цемента. Влиянию Li2O на формирование портландцементного клинкера в лабораторных условиях посвящено данное исследование; оно расширяет современные знания о влиянии этого оксида на фазовый состав и структуру клинкера. Кроме того, изучались свойства цементов, приготовленных из клинкеров, легированных литием. В качестве методов исследования применялись рентгеновская дифракция, дифференциально-термический анализ (ДТА), оптическая и электронная микроскопия. В частности, установлено, что Li2O, в зависимости от его содержания и скорости охлаждения клинкера, способствует разложению алита до микрокристаллической смеси белита и СаО. Цементы с обычными характеристиками можно приготовить из клинкеров, синтезированных при температуре 1350 °C и содержащих до 1 % масс. Li2O.

Název v anglickém jazyce

Influence of lithium on the formation and properties of Portland cement clinker

Popis výsledku anglicky

Lithium consumption in the production of batteries and accumulators for energy storage is increasing. It can be foreseen that the amount of waste with higher content of this metal will grow. Since cement production is one of the main users of secondary and waste raw materials on a mass scale, it is desirable to monitor the impact of this element on the properties of clinker and cement. In laboratory conditions, the effect of minor oxide - Li2O on formation of Portland cement clinker was observed. The research deepens the current knowledge about the effect of this oxide on phase composition and structure of clinker. Last but not least, the influence on the technological parameters of cements prepared from Li doped clinkers was also observed. X-ray diffraction, DTA, optical and electron microscopy were employed as research methods. Among other things, it has been found that Li2O causes the decomposition of the alite, the major clinker phase, to a microcrystalline mixture of belite and free lime, depending on its content and clinker cooling rate. Moreover, cements with sufficient technological parameters were prepared from clinkers burned at 1350 °C with Li2O up to 1 wt.%.

Druh

J_ost - Ostatní články v recenzovaných periodicích

CEP obor

—

OECD FORD obor

20500 - Materials engineering

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2019

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Цемент и его применение

ISSN

1607-8837

e-ISSN

—

Svazek periodika

2019

Číslo periodika v rámci svazku

6

Stát vydavatele periodika

RU - Ruská federace

Počet stran výsledku

5

Strana od-do

94-99

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—