High strength steel microstructures and properties after laser welding

Popis výsledku v původním jazyce

The paper presents metallographic observations of welded joints in high-strength steels. It brings a comparison of changes in material microstructure upon laser welding and upon MAG welding (Metal Active Gas). The size of the heat-affected zone (HAZ) wasone order of magnitude smaller and the grain considerably finer in case of the laser beam welding. This is also reflected in resulting properties of these joints. The strength of a laser-welded joint in the material Docol 1200M remains basically equal to that of the parent metal, whereas the strength of the MAG welded joint was about one half lower. In case of failure the MAG welds typically fracture along the border between the HAZ and the parent metal, while failure in laser welds occurs along the fusion line.

Název v anglickém jazyce

High strength steel microstructures and properties after laser welding

Popis výsledku anglicky

The paper presents metallographic observations of welded joints in high-strength steels. It brings a comparison of changes in material microstructure upon laser welding and upon MAG welding (Metal Active Gas). The size of the heat-affected zone (HAZ) wasone order of magnitude smaller and the grain considerably finer in case of the laser beam welding. This is also reflected in resulting properties of these joints. The strength of a laser-welded joint in the material Docol 1200M remains basically equal to that of the parent metal, whereas the strength of the MAG welded joint was about one half lower. In case of failure the MAG welds typically fracture along the border between the HAZ and the parent metal, while failure in laser welds occurs along the fusion line.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JP - Průmyslové procesy a zpracování

OECD FORD obor

—

Projekt

<a href="/cs/project/FR-TI1%2F363" target="_blank" >FR-TI1/363: *Výzkum a vývoj lehkého, bezpečného a ergonomického železničního sedadla</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Acta Metallurgica Slovaca

ISSN

1338-1660

e-ISSN

—

Svazek periodika

14

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

SK - Slovenská republika

Počet stran výsledku

5

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—