Grain refinement of low karbon steel by ECAP severe plastic deformation
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26316919%3A_____%2F11%3A%230000305" target="_blank" >RIV/26316919:_____/11:#0000305 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Grain refinement of low karbon steel by ECAP severe plastic deformation
Popis výsledku v původním jazyce
The aim of this work is to evaluate the effect of initial structure modification and increased temperature on ultrafine grain structure formation of commercial low carbon steel AISI 1014. Two different initial structural states of the steel were preparedusing thermal and thermomechanical treatment. The purpose of thermomechanical treatment was to refine the initial grain size in steel. The ultrafine grain structure was prepared by applying method severe plastic deformation ECAP with different level ofstraining at increased temperature. The impact of different effective strain ?ef introduced upon microstructure changes was investigated using light, scanning (SEM) and transmission electron microscopy (TEM) methods. The microhardness results (HV) alongthe deformed supported the microstructure development. Repeating deformation procedure (Bc) the coarse and modified (by TM) ferrite grains were refined and resulting structure was the mixture of fine grains having high angle boundaries. T
Název v anglickém jazyce
Grain refinement of low karbon steel by ECAP severe plastic deformation
Popis výsledku anglicky
The aim of this work is to evaluate the effect of initial structure modification and increased temperature on ultrafine grain structure formation of commercial low carbon steel AISI 1014. Two different initial structural states of the steel were preparedusing thermal and thermomechanical treatment. The purpose of thermomechanical treatment was to refine the initial grain size in steel. The ultrafine grain structure was prepared by applying method severe plastic deformation ECAP with different level ofstraining at increased temperature. The impact of different effective strain ?ef introduced upon microstructure changes was investigated using light, scanning (SEM) and transmission electron microscopy (TEM) methods. The microhardness results (HV) alongthe deformed supported the microstructure development. Repeating deformation procedure (Bc) the coarse and modified (by TM) ferrite grains were refined and resulting structure was the mixture of fine grains having high angle boundaries. T
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JQ - Strojní zařízení a nástroje
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
NANOCON 2011 CONFERENCE PROCEEDINGS, 3rd Int. Conference
ISBN
978-80-87294-27-7
ISSN
—
e-ISSN
—
Počet stran výsledku
8
Strana od-do
31-38
Název nakladatele
Tanger spol. s r.o.
Místo vydání
Ostrava, ČR
Místo konání akce
Brno, ČR
Datum konání akce
21. 8. 2011
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—