Accelerated carbide spheroidisation of bearing steel by induction heating

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26316919%3A_____%2F14%3A%230000596" target="_blank" >RIV/26316919:_____/14:#0000596 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.scopus.com/inward/record.url?eid=2-s2.0-84915784577&partnerID=40&md5=1fb17c4616229ab27c2e60d150436ab1" target="_blank" >http://www.scopus.com/inward/record.url?eid=2-s2.0-84915784577&partnerID=40&md5=1fb17c4616229ab27c2e60d150436ab1</a>

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Accelerated carbide spheroidisation of bearing steel by induction heating

Popis výsledku v původním jazyce

New type of thermal treatment for carbide spheroidisation was developed in COMTES FHT. Conventional heat treatment for carbide spheroidisation consists in long annealing at temperatures around temperature A1. Diffusion based process of pearlite shape transformation from lamellar to globular morphology takes usually several hours with subsequent cooling in furnace. The new heat treatment was performed using induction heating allowing rapid heating and thus rapid structure changes. Accelerated carbide spheroidisation principle is based on fast temperature cycling around transformation temperature A1. The purpose of this annealing process is to obtain globular carbides uniformly distributed in the matrix and to achieve overall softening in several minutes. The present paper explores the effect of the newly-designed thermal schedules on the cementite lamellae fragmentation, on the decrease in hardness in bearing steel grade 100CrMnSi6-4 and on processing times.

Název v anglickém jazyce

Accelerated carbide spheroidisation of bearing steel by induction heating

Popis výsledku anglicky

New type of thermal treatment for carbide spheroidisation was developed in COMTES FHT. Conventional heat treatment for carbide spheroidisation consists in long annealing at temperatures around temperature A1. Diffusion based process of pearlite shape transformation from lamellar to globular morphology takes usually several hours with subsequent cooling in furnace. The new heat treatment was performed using induction heating allowing rapid heating and thus rapid structure changes. Accelerated carbide spheroidisation principle is based on fast temperature cycling around transformation temperature A1. The purpose of this annealing process is to obtain globular carbides uniformly distributed in the matrix and to achieve overall softening in several minutes. The present paper explores the effect of the newly-designed thermal schedules on the cementite lamellae fragmentation, on the decrease in hardness in bearing steel grade 100CrMnSi6-4 and on processing times.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/LF13032" target="_blank" >LF13032: Vývoj metod tepelně-chemického zpracování ocelí s využitím fluidního lože s termoaktivními prášky</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

European Conference on Heat Treatment and 21st IFHTSE Congress

ISBN

9780000000002

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

357-364

Název nakladatele

Arbeitsgemeineschaft Warmebehandlung u. Werkstofftechnik

Místo vydání

Bremen

Místo konání akce

Munich

Datum konání akce

12. 5. 2014

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—