Investigation of Sample-size Influence on Tensile Test Results at Different Strain Rates

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26316919%3A_____%2F15%3A%230000634" target="_blank" >RIV/26316919:_____/15:#0000634 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.sciencedirect.com/science/article/pii/S1877705815017257" target="_blank" >http://www.sciencedirect.com/science/article/pii/S1877705815017257</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.proeng.2015.08.086" target="_blank" >10.1016/j.proeng.2015.08.086</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Investigation of Sample-size Influence on Tensile Test Results at Different Strain Rates

Popis výsledku v původním jazyce

The paper deals with the determination of dynamic mechanical properties of steel sheets by the miniature testing technique. Several materials were investigated, namely S235, S355 and 1.4301. The newly developed micro-tensile test (M-TT) allows local mechanical properties measurement which can be successfully used for example for weld heterogeneity determination. Furthermore, due to small size samples (tensile sample gauge section dimension of 0,5x1,5x3 mm), much higher strain rates can be attained usingrelatively slow loading velocities in comparison to standard dynamic tests resulting in high results consistency thanks to significant reduction of the oscillations which are typical for common high strain rate tests. The results obtained from M-TT andstandard tensile tests were compared.

Název v anglickém jazyce

Investigation of Sample-size Influence on Tensile Test Results at Different Strain Rates

Popis výsledku anglicky

The paper deals with the determination of dynamic mechanical properties of steel sheets by the miniature testing technique. Several materials were investigated, namely S235, S355 and 1.4301. The newly developed micro-tensile test (M-TT) allows local mechanical properties measurement which can be successfully used for example for weld heterogeneity determination. Furthermore, due to small size samples (tensile sample gauge section dimension of 0,5x1,5x3 mm), much higher strain rates can be attained usingrelatively slow loading velocities in comparison to standard dynamic tests resulting in high results consistency thanks to significant reduction of the oscillations which are typical for common high strain rate tests. The results obtained from M-TT andstandard tensile tests were compared.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Procedia Engineering

ISSN

1877-7058

e-ISSN

—

Svazek periodika

114/2015

Číslo periodika v rámci svazku

14.9.2015

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

6

Strana od-do

410-415

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—