Corrosion testing of nickel alloy for molten salt reactors

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26316919%3A_____%2F15%3A%230000646" target="_blank" >RIV/26316919:_____/15:#0000646 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/26722445:_____/15:N0000002

Výsledek na webu

<a href="http://www.journalamme.org/vol70_2/7024.pdf" target="_blank" >http://www.journalamme.org/vol70_2/7024.pdf</a>

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Corrosion testing of nickel alloy for molten salt reactors

Popis výsledku v původním jazyce

The nickel alloys are determined for modern conceptions of nuclear reactors in which molten fluoride salts are used in the primary and/or secondary circuit as coolants. Particularly MONICR alloy represents a material alternative with high corrosion resistance in the area of fluoride salts and it has very good creep properties in the temperature range of 650 ? 750 °C as well. Article deals with corrosion test conducted in LiF ? BeF2 molten salt at 700 °C using nitrogen as the inert atmosphere with the test durations of 1 and 3 months. The results shows that chromium and molybdenum are preferentially released into the melt and the surface and grain boundaries become depleted of chromium.

Název v anglickém jazyce

Corrosion testing of nickel alloy for molten salt reactors

Popis výsledku anglicky

The nickel alloys are determined for modern conceptions of nuclear reactors in which molten fluoride salts are used in the primary and/or secondary circuit as coolants. Particularly MONICR alloy represents a material alternative with high corrosion resistance in the area of fluoride salts and it has very good creep properties in the temperature range of 650 ? 750 °C as well. Article deals with corrosion test conducted in LiF ? BeF2 molten salt at 700 °C using nitrogen as the inert atmosphere with the test durations of 1 and 3 months. The results shows that chromium and molybdenum are preferentially released into the melt and the surface and grain boundaries become depleted of chromium.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Achievements in Materials and Manufacturing Engineering

ISSN

1734-8412

e-ISSN

—

Svazek periodika

70

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

PL - Polská republika

Počet stran výsledku

8

Strana od-do

78-85

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—