Influence of rotary swaging and subsequent age hardening on properties of EN AW 6082 aluminium alloy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26316919%3A_____%2F17%3AN0000023" target="_blank" >RIV/26316919:_____/17:N0000023 - isvavai.cz</a>

Výsledek na webu

<a href="http://iopscience.iop.org/article/10.1088/1757-899X/179/1/012049" target="_blank" >http://iopscience.iop.org/article/10.1088/1757-899X/179/1/012049</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1088/1757-899X/179/1/012049" target="_blank" >10.1088/1757-899X/179/1/012049</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Influence of rotary swaging and subsequent age hardening on properties of EN AW 6082 aluminium alloy

Popis výsledku v původním jazyce

Mechanical properties and microstructure of EN AW 6082 were investigated. The aluminium alloy was processed by combining the solution annealing, plastic deformation and artificial age hardening, respectively. The initial state of the investigated material was provided in the form of extruded rods with the diameter of 12 mm. For the solution annealing the temperature 530 °C was chosen. The plastic deformation was realized by rotary swaging at ambient temperature and the investigated material was rotary swaged from 12 to 10 mm in diameter. The effect of the age hardening temperature and time was studied at temperatures of 120 and 160 °C and times 1 - 12 hours. The impact of processing parameters on mechanical properties was assessed by tensile testing and hardness measurement. Metallographic examination was carried out by light optical microscopy (LOM) and scanning electron microscopy using electron backscatter diffraction (SEM-EBSD).

Název v anglickém jazyce

Influence of rotary swaging and subsequent age hardening on properties of EN AW 6082 aluminium alloy

Popis výsledku anglicky

Mechanical properties and microstructure of EN AW 6082 were investigated. The aluminium alloy was processed by combining the solution annealing, plastic deformation and artificial age hardening, respectively. The initial state of the investigated material was provided in the form of extruded rods with the diameter of 12 mm. For the solution annealing the temperature 530 °C was chosen. The plastic deformation was realized by rotary swaging at ambient temperature and the investigated material was rotary swaged from 12 to 10 mm in diameter. The effect of the age hardening temperature and time was studied at temperatures of 120 and 160 °C and times 1 - 12 hours. The impact of processing parameters on mechanical properties was assessed by tensile testing and hardness measurement. Metallographic examination was carried out by light optical microscopy (LOM) and scanning electron microscopy using electron backscatter diffraction (SEM-EBSD).

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

<a href="/cs/project/LO1412" target="_blank" >LO1412: Rozvoj Západočeského materiálově metalurgického Centra</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

4th International Conference Recent Trends in Structural Materials (COMAT 2016)

ISBN

—

ISSN

1757-8981

e-ISSN

—

Počet stran výsledku

6

Strana od-do

nestránkováno

Název nakladatele

IOP Publishing

Místo vydání

Bristol

Místo konání akce

Plzeň

Datum konání akce

9. 11. 2016

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000403407100049