Anisotropy of Thermal Expansion in an AZ31 Magnesium Alloy Subjected to the Accumulative Roll Bonding

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26316919%3A_____%2F18%3AN0000019" target="_blank" >RIV/26316919:_____/18:N0000019 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/26316919:_____/18:N0000018 RIV/00216208:11320/18:10383785

Výsledek na webu

<a href="http://przyrbwn.icm.edu.pl/APP/PDF/134/app134z3p47.pdf" target="_blank" >http://przyrbwn.icm.edu.pl/APP/PDF/134/app134z3p47.pdf</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.12693/APhysPolA.134.820" target="_blank" >10.12693/APhysPolA.134.820</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Anisotropy of Thermal Expansion in an AZ31 Magnesium Alloy Subjected to the Accumulative Roll Bonding

Popis výsledku v původním jazyce

Accumulative roll bonding is one of method for the production of metal materials with ultrafine grain microstructure. Sheets of the AZ31 magnesium alloy subjected to the 1 and 2 accumulative roll bonding passes through the rolling mill were cut so that the sample axis was either parallel or perpendicular to the rolling direction. The linear thermal expansion of samples was measured using a LINSEIS L75PT-1600 dilatometer in the temperature range from room temperature up to 400 degrees C. The thermal expansion curves of the sheets were measured during two consequent heating and cooling cycles. The temperature dependences of the relative elongation and of the thermal expansion coefficient were estimated from the dilatometer measurements. Planar anisotropy of the thermal expansion was found.

Název v anglickém jazyce

Anisotropy of Thermal Expansion in an AZ31 Magnesium Alloy Subjected to the Accumulative Roll Bonding

Popis výsledku anglicky

Accumulative roll bonding is one of method for the production of metal materials with ultrafine grain microstructure. Sheets of the AZ31 magnesium alloy subjected to the 1 and 2 accumulative roll bonding passes through the rolling mill were cut so that the sample axis was either parallel or perpendicular to the rolling direction. The linear thermal expansion of samples was measured using a LINSEIS L75PT-1600 dilatometer in the temperature range from room temperature up to 400 degrees C. The thermal expansion curves of the sheets were measured during two consequent heating and cooling cycles. The temperature dependences of the relative elongation and of the thermal expansion coefficient were estimated from the dilatometer measurements. Planar anisotropy of the thermal expansion was found.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2018

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

ACTA PHYSICA POLONICA A

ISSN

0587-4246

e-ISSN

1898-794X

Svazek periodika

134

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

PL - Polská republika

Počet stran výsledku

4

Strana od-do

820-823

Kód UT WoS článku

000453257500048

EID výsledku v databázi Scopus

2-s2.0-85040099012