Beta phase stability of Ti-35Nb-6Ta-7Zr-0.7O beta titanium alloy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26316919%3A_____%2F18%3AN0000061" target="_blank" >RIV/26316919:_____/18:N0000061 - isvavai.cz</a>

Výsledek na webu

<a href="http://iopscience.iop.org/article/10.1088/1757-899X/461/1/012068" target="_blank" >http://iopscience.iop.org/article/10.1088/1757-899X/461/1/012068</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1088/1757-899X/461/1/012068" target="_blank" >10.1088/1757-899X/461/1/012068</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Beta phase stability of Ti-35Nb-6Ta-7Zr-0.7O beta titanium alloy

Popis výsledku v původním jazyce

Phase stability of metastable beta Ti alloy Ti-35Nb-6Ta-7Zr-0.7O (wt.%) in a beta solution treated condition was studied during annealing at 400°C – 700°C for 1 h – 16 h. Resulting micro structure was characterized by scanning electron microscopy; the samples were also characterized by microhardness measurements. The microhardness did not change in any of the annealed condition. The reason follows from the microstructural observations, the ? phase precipitation did occur only at the grain boundaries and only at higher temperatures / longer annealing times. Thus, the ß phase stability is high and this fact can be used for designing annealing treatments or the thermo-mechanical processing route.

Název v anglickém jazyce

Beta phase stability of Ti-35Nb-6Ta-7Zr-0.7O beta titanium alloy

Popis výsledku anglicky

Phase stability of metastable beta Ti alloy Ti-35Nb-6Ta-7Zr-0.7O (wt.%) in a beta solution treated condition was studied during annealing at 400°C – 700°C for 1 h – 16 h. Resulting micro structure was characterized by scanning electron microscopy; the samples were also characterized by microhardness measurements. The microhardness did not change in any of the annealed condition. The reason follows from the microstructural observations, the ? phase precipitation did occur only at the grain boundaries and only at higher temperatures / longer annealing times. Thus, the ß phase stability is high and this fact can be used for designing annealing treatments or the thermo-mechanical processing route.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

<a href="/cs/project/FV20147" target="_blank" >FV20147: Nová generace kloubních implantátů vyrobených z beta slitiny Ti</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2018

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

5th International Conference Recent Trends in Structural Materials, COMAT 2018

ISBN

—

ISSN

1757-899X

e-ISSN

—

Počet stran výsledku

6

Strana od-do

nestránkováno

Název nakladatele

IOP Publishing Ltd.

Místo vydání

Bristol

Místo konání akce

Plzeň

Datum konání akce

14. 11. 2018

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—