Mechanical and Microstructural Properties of Rotary-Swaged Wire of Commercial-Purity Titanium

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26316919%3A_____%2F19%3AN0000010" target="_blank" >RIV/26316919:_____/19:N0000010 - isvavai.cz</a>
Výsledek na webu
<a href="https://publications.waset.org/10010561/mechanical-and-microstructural-properties-of-rotary-swaged-wire-of-commercial-purity-titanium" target="_blank" >https://publications.waset.org/10010561/mechanical-and-microstructural-properties-of-rotary-swaged-wire-of-commercial-purity-titanium</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.5281/zenodo.3300423" target="_blank" >10.5281/zenodo.3300423</a>

Jazyk výsledku
angličtina
Název v původním jazyce
Mechanical and Microstructural Properties of Rotary-Swaged Wire of Commercial-Purity Titanium
Popis výsledku v původním jazyce
Bars made of titanium grade 2 and grade 4 were subjected to rotary forging with up to 2.2 true strain reduction in the cross-section from 10 to 3.81 mm. During progressive deformation, grain refinement in the transverse direction took place. In the longitudinal direction, ultrafine microstructure has not developed. It has been demonstrated that titanium grade 2 strengthens more than grade 4. The ultimate tensile strength increased from 650 MPa to 1040 MPa in titanium grade 4. Hardness profiles on the cross section in both materials show an increase in the centre of the wire.
Název v anglickém jazyce
Mechanical and Microstructural Properties of Rotary-Swaged Wire of Commercial-Purity Titanium
Popis výsledku anglicky
Bars made of titanium grade 2 and grade 4 were subjected to rotary forging with up to 2.2 true strain reduction in the cross-section from 10 to 3.81 mm. During progressive deformation, grain refinement in the transverse direction took place. In the longitudinal direction, ultrafine microstructure has not developed. It has been demonstrated that titanium grade 2 strengthens more than grade 4. The ultimate tensile strength increased from 650 MPa to 1040 MPa in titanium grade 4. Hardness profiles on the cross section in both materials show an increase in the centre of the wire.

Projekt
<a href="/cs/project/LO1412" target="_blank" >LO1412: Rozvoj Západočeského materiálově metalurgického Centra</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění
2019
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika
International Journal of Materials and Metallurgical Engineering
ISSN
1307-6892
e-ISSN
—
Svazek periodika
13
Číslo periodika v rámci svazku
7
Stát vydavatele periodika
TR - Turecká republika
Počet stran výsledku
5
Strana od-do
327-331
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—

Podobné výsledky(10)