Strain Hardening in an AZ31 Alloy Submitted to Rotary Swaging
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26316919%3A_____%2F21%3AN0000002" target="_blank" >RIV/26316919:_____/21:N0000002 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/00216208:11320/21:10438129
Výsledek na webu
<a href="https://www.mdpi.com/1996-1944/14/1/157/htm" target="_blank" >https://www.mdpi.com/1996-1944/14/1/157/htm</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.3390/ma14010157" target="_blank" >10.3390/ma14010157</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Strain Hardening in an AZ31 Alloy Submitted to Rotary Swaging
Popis výsledku v původním jazyce
An extruded magnesium AZ31 magnesium alloy was processed by rotary swaging (RSW) and then deformed by tension and compression at room temperature. The work-hardening behaviour of 1–5 times swaged samples was analysed using Kocks-Mecking plots. Accumulation of dislocations on dislocation obstacles and twin boundaries is the deciding factor for the strain hardening. Profuse twinning in compression seems to be the reason for the higher hardening observed during compression. The main softening mechanism is apparently the cross-slip between the pyramidal planes of the second and first order. A massive twinning observed at the deformation beginning influences the Hall-Petch parameters.
Název v anglickém jazyce
Strain Hardening in an AZ31 Alloy Submitted to Rotary Swaging
Popis výsledku anglicky
An extruded magnesium AZ31 magnesium alloy was processed by rotary swaging (RSW) and then deformed by tension and compression at room temperature. The work-hardening behaviour of 1–5 times swaged samples was analysed using Kocks-Mecking plots. Accumulation of dislocations on dislocation obstacles and twin boundaries is the deciding factor for the strain hardening. Profuse twinning in compression seems to be the reason for the higher hardening observed during compression. The main softening mechanism is apparently the cross-slip between the pyramidal planes of the second and first order. A massive twinning observed at the deformation beginning influences the Hall-Petch parameters.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
—
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2021
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
MATERIALS
ISSN
1996-1944
e-ISSN
1996-1944
Svazek periodika
14
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
17
Strana od-do
nestránkováno
Kód UT WoS článku
000606052200001
EID výsledku v databázi Scopus
2-s2.0-85099143316