High Manganese TWIP Steel with Increased Corrosion Resistance
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26316919%3A_____%2F22%3AN0000033" target="_blank" >RIV/26316919:_____/22:N0000033 - isvavai.cz</a>
Výsledek na webu
<a href="https://www.mdpi.com/2075-4701/12/10/1765" target="_blank" >https://www.mdpi.com/2075-4701/12/10/1765</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.3390/met12101765" target="_blank" >10.3390/met12101765</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
High Manganese TWIP Steel with Increased Corrosion Resistance
Popis výsledku v původním jazyce
The paper describes the development of austenitic steel with the TWIP effect, which is alloyed with chromium to increase corrosion resistance. The experimental heat of this steel was cast in an experimental melting furnace and subsequently subjected to hot and cold rolling. After cold rolling, the appropriate recrystallization annealing temperature was applied to obtain the optimal austenitic grain size. X-ray diffraction proved that the steel contains a fully austenitic structure. After recrystallization annealing, the sheets achieved a TS of more than 950 MPa with an elongation of 40%. The corrosion resistance of this steel is increased with the addition of chromium.
Název v anglickém jazyce
High Manganese TWIP Steel with Increased Corrosion Resistance
Popis výsledku anglicky
The paper describes the development of austenitic steel with the TWIP effect, which is alloyed with chromium to increase corrosion resistance. The experimental heat of this steel was cast in an experimental melting furnace and subsequently subjected to hot and cold rolling. After cold rolling, the appropriate recrystallization annealing temperature was applied to obtain the optimal austenitic grain size. X-ray diffraction proved that the steel contains a fully austenitic structure. After recrystallization annealing, the sheets achieved a TS of more than 950 MPa with an elongation of 40%. The corrosion resistance of this steel is increased with the addition of chromium.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/EF16_019%2F0000836" target="_blank" >EF16_019/0000836: Výzkum pokročilých ocelí s unikátními vlastnostmi</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2022
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
METALS
ISSN
2075-4701
e-ISSN
2075-4701
Svazek periodika
12
Číslo periodika v rámci svazku
10
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
8
Strana od-do
nestránkováno
Kód UT WoS článku
000873103800001
EID výsledku v databázi Scopus
2-s2.0-85140978803