Fracture toughness of the hydrogen charged EUROFER 97 RAFM steel at room temperature and 120 degrees C
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26722445%3A_____%2F09%3A%230000518" target="_blank" >RIV/26722445:_____/09:#0000518 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.jnucmat.2009.03.053" target="_blank" >http://dx.doi.org/10.1016/j.jnucmat.2009.03.053</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.jnucmat.2009.03.053" target="_blank" >10.1016/j.jnucmat.2009.03.053</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Fracture toughness of the hydrogen charged EUROFER 97 RAFM steel at room temperature and 120 degrees C
Popis výsledku v původním jazyce
The static fracture toughness of EUROFER 97 reduced activation ferritic-martensitic steel was investigated in presence of higher content of hydrogen. The hydrogen effect is shown during fracture toughness testing both of base and weld metals at room temperature and at 120°C. At the room temperature testing the J0.2 integral values will decrease depending on hydrogen content in the range of 2 -4 wppm. The same hydrogen content of 2 wppm manifests itself by an uneven level of hydrogen embrittlement for base metal and weld metal.
Název v anglickém jazyce
Fracture toughness of the hydrogen charged EUROFER 97 RAFM steel at room temperature and 120 degrees C
Popis výsledku anglicky
The static fracture toughness of EUROFER 97 reduced activation ferritic-martensitic steel was investigated in presence of higher content of hydrogen. The hydrogen effect is shown during fracture toughness testing both of base and weld metals at room temperature and at 120°C. At the room temperature testing the J0.2 integral values will decrease depending on hydrogen content in the range of 2 -4 wppm. The same hydrogen content of 2 wppm manifests itself by an uneven level of hydrogen embrittlement for base metal and weld metal.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
20301 - Mechanical engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/2A-1TP1%2F100" target="_blank" >2A-1TP1/100: Vysokoteplotní plynové systémy.</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2009
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of nuclear materials
ISSN
0022-3115
e-ISSN
—
Svazek periodika
392
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
NL - Nizozemsko
Počet stran výsledku
8
Strana od-do
—
Kód UT WoS článku
000267906500020
EID výsledku v databázi Scopus
—