Fatigue performance of blade steel T552 in a corrosive environment

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26722445%3A_____%2F16%3AN0000097" target="_blank" >RIV/26722445:_____/16:N0000097 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/26722445:_____/16:N0000038

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Fatigue performance of blade steel T552 in a corrosive environment

Popis výsledku v původním jazyce

This contribution is based on an experimental programme which deals with the issue of blade steel T552 corrosion fatigue damage. The specimens were taken from a reference material delivered for blade production and tested in a corrosion cell under pre-stress of 300 MPa. A chloride solution of 35 ppm was chosen as the environment at a temperature of 80°C. Such an environment can be considered as the limit state that should not occur during the operating regime. The results are summarized and compared with experiments conducted at another workplace.

Název v anglickém jazyce

Fatigue performance of blade steel T552 in a corrosive environment

Popis výsledku anglicky

This contribution is based on an experimental programme which deals with the issue of blade steel T552 corrosion fatigue damage. The specimens were taken from a reference material delivered for blade production and tested in a corrosion cell under pre-stress of 300 MPa. A chloride solution of 35 ppm was chosen as the environment at a temperature of 80°C. Such an environment can be considered as the limit state that should not occur during the operating regime. The results are summarized and compared with experiments conducted at another workplace.

Druh

D - Stať ve sborníku

CEP obor

JF - Jaderná energetika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

4th International Conference Recent Trends in Structural Materials

ISBN

978-80-87294-69-7

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

1-6

Název nakladatele

Tanger Ltd

Místo vydání

Ostrava

Místo konání akce

Plzeň

Datum konání akce

9. 11. 2016

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—