Pitting corrosion on steam turbine blades steels

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26722445%3A_____%2F16%3AN0000113" target="_blank" >RIV/26722445:_____/16:N0000113 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/26722445:_____/16:N0000114

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Pitting corrosion on steam turbine blades steels

Popis výsledku v původním jazyce

Pitting corrosion on steam turbine blades become significant problem. Corrosion pits are often places of fatigue crack initiation. This sort of degradation is often observed on last stages of the turbine, where steam condensation occurs. This paper shows results of corrosion resistance measurement on two different steels that are usually used for manufacturing blades on steam turbine last stages. Corrosion behaviour of steel Böhler T552 and Böhler T671 was tested in 35ppm chloride solution. The environment was chosen to emulate worst possible conditions, common chloride concentration is much lower. Determination of pitting corrosion resistance was done by electrochemical cyclic polarisation. In case of T552 steel was also influence of heat treatment investigated.

Název v anglickém jazyce

Pitting corrosion on steam turbine blades steels

Popis výsledku anglicky

Pitting corrosion on steam turbine blades become significant problem. Corrosion pits are often places of fatigue crack initiation. This sort of degradation is often observed on last stages of the turbine, where steam condensation occurs. This paper shows results of corrosion resistance measurement on two different steels that are usually used for manufacturing blades on steam turbine last stages. Corrosion behaviour of steel Böhler T552 and Böhler T671 was tested in 35ppm chloride solution. The environment was chosen to emulate worst possible conditions, common chloride concentration is much lower. Determination of pitting corrosion resistance was done by electrochemical cyclic polarisation. In case of T552 steel was also influence of heat treatment investigated.

Druh

D - Stať ve sborníku

CEP obor

JF - Jaderná energetika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Utilization of SUSEN Technologies for the Gen IV Development

ISBN

978-80-270-0925-1

ISSN

—

e-ISSN

—

Počet stran výsledku

3

Strana od-do

104-106

Název nakladatele

Centrum výzkumu Řež, s.r.o.

Místo vydání

Řež

Místo konání akce

Řež

Datum konání akce

24. 11. 2016

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—