Transformation Pathway upon Heating of Metastable beta Titanium Alloy Ti-15Mo Investigated by Neutron Diffraction
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26722445%3A_____%2F19%3AN0000055" target="_blank" >RIV/26722445:_____/19:N0000055 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/61389005:_____/19:00518767 RIV/61388998:_____/19:00518767 RIV/00216208:11320/19:10405671
Výsledek na webu
<a href="https://www.mdpi.com/1996-1944/12/21/3570" target="_blank" >https://www.mdpi.com/1996-1944/12/21/3570</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.3390/ma12213570" target="_blank" >10.3390/ma12213570</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Transformation Pathway upon Heating of Metastable beta Titanium Alloy Ti-15Mo Investigated by Neutron Diffraction
Popis výsledku v původním jazyce
A transformation pathway during thermal treatment of metastable beta Ti-15Mo alloy was investigated by in situ neutron diffraction. The evolution of individual phases alpha, beta, and omega was investigated during linear heating with two heating rates of 1.9 degrees C/min and 5 degrees C/min and during aging at 450 degrees C. The results showed that with a sufficient heating rate (5 degrees C/min in this case), the w phase dissolves before the alpha phase forms. On the other hand, for the slower heating rate of 1.9 degrees C/min, a small temperature interval of the coexistence of the alpha and omega phases was detected. Volume fractions and lattice parameters of all phases were also determined.
Název v anglickém jazyce
Transformation Pathway upon Heating of Metastable beta Titanium Alloy Ti-15Mo Investigated by Neutron Diffraction
Popis výsledku anglicky
A transformation pathway during thermal treatment of metastable beta Ti-15Mo alloy was investigated by in situ neutron diffraction. The evolution of individual phases alpha, beta, and omega was investigated during linear heating with two heating rates of 1.9 degrees C/min and 5 degrees C/min and during aging at 450 degrees C. The results showed that with a sufficient heating rate (5 degrees C/min in this case), the w phase dissolves before the alpha phase forms. On the other hand, for the slower heating rate of 1.9 degrees C/min, a small temperature interval of the coexistence of the alpha and omega phases was detected. Volume fractions and lattice parameters of all phases were also determined.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2019
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Materials
ISSN
1996-1944
e-ISSN
—
Svazek periodika
12
Číslo periodika v rámci svazku
21
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
16
Strana od-do
1-16
Kód UT WoS článku
000502798800111
EID výsledku v databázi Scopus
2-s2.0-85074649571