Microstructural Evaluation of Nickel Based Alloy Inconel 718 after Exposure in SCWL

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26722445%3A_____%2F20%3AN0000073" target="_blank" >RIV/26722445:_____/20:N0000073 - isvavai.cz</a>

Výsledek na webu

<a href="https://jadernaenergie.online/wp-content/uploads/2020/09/CVR_casopis_jaderna_energie_S.pdf" target="_blank" >https://jadernaenergie.online/wp-content/uploads/2020/09/CVR_casopis_jaderna_energie_S.pdf</a>

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Microstructural Evaluation of Nickel Based Alloy Inconel 718 after Exposure in SCWL

Popis výsledku v původním jazyce

Within the R4S project, material research in supercritical water was realised by exposures in Supercritical Water Loop (SCWL). One of tested material was Inconel 718 which is candidate alloy for the new type of Generation IV reactors (GIV), specifically Supercritical Water-Cooled Reactor (SCWR). Specimens were exposed to the demineralised water with temperature 395 °C and pressure 25 MPa for 1,000 hours. Scanning Electron Microscopy (SEM) with Energy Dispersive Spectroscopy (EDS) in combination with X-Ray Diffraction (XRD) were used to evaluate the microstructure of Inconel 718 after the exposure to supercritical water. All these methods confirmed a growth of crystals Iron Aluminum Chromium Oxide – hercynite and chromite Fe(Al,Cr)2O4 with average size of grain about 1 μm on the surface of specimens.

Název v anglickém jazyce

Microstructural Evaluation of Nickel Based Alloy Inconel 718 after Exposure in SCWL

Popis výsledku anglicky

Within the R4S project, material research in supercritical water was realised by exposures in Supercritical Water Loop (SCWL). One of tested material was Inconel 718 which is candidate alloy for the new type of Generation IV reactors (GIV), specifically Supercritical Water-Cooled Reactor (SCWR). Specimens were exposed to the demineralised water with temperature 395 °C and pressure 25 MPa for 1,000 hours. Scanning Electron Microscopy (SEM) with Energy Dispersive Spectroscopy (EDS) in combination with X-Ray Diffraction (XRD) were used to evaluate the microstructure of Inconel 718 after the exposure to supercritical water. All these methods confirmed a growth of crystals Iron Aluminum Chromium Oxide – hercynite and chromite Fe(Al,Cr)2O4 with average size of grain about 1 μm on the surface of specimens.

Druh

J_ost - Ostatní články v recenzovaných periodicích

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2020

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Jaderná energie

ISSN

2694-9024

e-ISSN

—

Svazek periodika

1(66)

Číslo periodika v rámci svazku

SI

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

5

Strana od-do

77-81

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—