Comparative high-field magnetization study of (Sm,er)2fe17 and er2fe17 compounds and their nitrides
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26722445%3A_____%2F21%3AN0000097" target="_blank" >RIV/26722445:_____/21:N0000097 - isvavai.cz</a>
Výsledek na webu
<a href="https://www.scientific.net/MSF.1037.148" target="_blank" >https://www.scientific.net/MSF.1037.148</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/MSF.1037.148" target="_blank" >10.4028/www.scientific.net/MSF.1037.148</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Comparative high-field magnetization study of (Sm,er)2fe17 and er2fe17 compounds and their nitrides
Popis výsledku v původním jazyce
Magnetic properties of the R2Fe17 compounds are sensitive to the atomic substitutions and interstitial absorption of nitrogen. In our work, both were combined and their effect on the magnetization behavior of Er2Fe17 compound in magnetic fields up to 58 T was studied. Er2Fe17N2, Sm1.2Er0.8Fe17N2 and Sm1.8Er0.2Fe17N2.1 nitrides were prepared. Magnetization measurements were carried out, mainly on powder samples (excluding Er2Fe17 single crystal). Nanopowders of Sm1.2Er0.8Fe17N2 were obtained by mechanical grinding. The grinding time was varied from 0 to 60 minutes. The strength of the inter-sublattice coupling in samples is estimated by analyzing high-field magnetization data. © 2021 Trans Tech Publications Ltd, Switzerland.
Název v anglickém jazyce
Comparative high-field magnetization study of (Sm,er)2fe17 and er2fe17 compounds and their nitrides
Popis výsledku anglicky
Magnetic properties of the R2Fe17 compounds are sensitive to the atomic substitutions and interstitial absorption of nitrogen. In our work, both were combined and their effect on the magnetization behavior of Er2Fe17 compound in magnetic fields up to 58 T was studied. Er2Fe17N2, Sm1.2Er0.8Fe17N2 and Sm1.8Er0.2Fe17N2.1 nitrides were prepared. Magnetization measurements were carried out, mainly on powder samples (excluding Er2Fe17 single crystal). Nanopowders of Sm1.2Er0.8Fe17N2 were obtained by mechanical grinding. The grinding time was varied from 0 to 60 minutes. The strength of the inter-sublattice coupling in samples is estimated by analyzing high-field magnetization data. © 2021 Trans Tech Publications Ltd, Switzerland.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/LQ1603" target="_blank" >LQ1603: Výzkum pro SUSEN</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2021
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Materials Science Forum, Volume 1037
ISBN
978-303571834-8
ISSN
0255-5476
e-ISSN
—
Počet stran výsledku
6
Strana od-do
148-153
Název nakladatele
Trans Tech Publications Ltd.
Místo vydání
Baech, Switzerland
Místo konání akce
Virtual, Online
Datum konání akce
1. 3. 2021
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—