Microscopic Evaluation of Protective Coating by Coated Sheet safter Corrosion Load

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F44555601%3A13420%2F12%3A43884448" target="_blank" >RIV/44555601:13420/12:43884448 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Microscopic Evaluation of Protective Coating by Coated Sheet safter Corrosion Load

Popis výsledku v původním jazyce

Introduction into problems - The aim of the paper was microscopically analyze protective layer by coated sheets after corrosion loading which were pre-treated by various ways. The samples were divided into 4 groups according to the pretreatment type andduration of corrosion load. After a corrosive effect on the corrosion chamber the protective layer was subjected to microscopic evaluation. For samples of group I and IV have to degrade the protective layer and the formation of corrosion products on thebase material which causes degradation of the protective layer and shorten its life. For samples of group II and III microstructural analysis showed good condition of the painted surface layer and the base material showed no presence of corrosion products. It again confirms the need for compliance of technological conditions for the pretreatment of the surface particularly in the application of modern less aggressive means.

Název v anglickém jazyce

Microscopic Evaluation of Protective Coating by Coated Sheet safter Corrosion Load

Popis výsledku anglicky

Introduction into problems - The aim of the paper was microscopically analyze protective layer by coated sheets after corrosion loading which were pre-treated by various ways. The samples were divided into 4 groups according to the pretreatment type andduration of corrosion load. After a corrosive effect on the corrosion chamber the protective layer was subjected to microscopic evaluation. For samples of group I and IV have to degrade the protective layer and the formation of corrosion products on thebase material which causes degradation of the protective layer and shorten its life. For samples of group II and III microstructural analysis showed good condition of the painted surface layer and the base material showed no presence of corrosion products. It again confirms the need for compliance of technological conditions for the pretreatment of the surface particularly in the application of modern less aggressive means.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JK - Koroze a povrchové úpravy materiálu

OECD FORD obor

—

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Manufacturing Technology

ISSN

1213-2489

e-ISSN

—

Svazek periodika

12

Číslo periodika v rámci svazku

13

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

7

Strana od-do

151-157

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—