Study of the structure and fluidity of alloy of the AlSiMg system with a different calcium content

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F44555601%3A13420%2F13%3A43885461" target="_blank" >RIV/44555601:13420/13:43885461 - isvavai.cz</a>

Výsledek na webu

<a href="http://link.springer.com/article/10.1007%2Fs11015-013-9639-7#" target="_blank" >http://link.springer.com/article/10.1007%2Fs11015-013-9639-7#</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1007/s11015-013-9639-7" target="_blank" >10.1007/s11015-013-9639-7</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Study of the structure and fluidity of alloy of the AlSiMg system with a different calcium content

Popis výsledku v původním jazyce

The effect of calcium in an amount of 0.1-1.0% on aluminum alloy modification with the aim of revealing the optimum composition in order to achieve required properties is studied. New aluminum alloys and their production properties (fluidity and processing capacity), chemical properties (corrosion resistance), and also mechanical properties (ultimate breaking strength, ductility, relative elongation, and hardness), are studied. General structural analysis is performed providing identification of individual components and new calcium compounds in aluminum alloy.

Název v anglickém jazyce

Study of the structure and fluidity of alloy of the AlSiMg system with a different calcium content

Popis výsledku anglicky

The effect of calcium in an amount of 0.1-1.0% on aluminum alloy modification with the aim of revealing the optimum composition in order to achieve required properties is studied. New aluminum alloys and their production properties (fluidity and processing capacity), chemical properties (corrosion resistance), and also mechanical properties (ultimate breaking strength, ductility, relative elongation, and hardness), are studied. General structural analysis is performed providing identification of individual components and new calcium compounds in aluminum alloy.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Metallurgist

ISSN

0026-0894

e-ISSN

—

Svazek periodika

2013

Číslo periodika v rámci svazku

56

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

6

Strana od-do

708-713

Kód UT WoS článku

000289694900010

EID výsledku v databázi Scopus

—