Research of Corrosion Properties of Al-Si Alloys Antimony Alloyed
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F44555601%3A13420%2F13%3A43885506" target="_blank" >RIV/44555601:13420/13:43885506 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Research of Corrosion Properties of Al-Si Alloys Antimony Alloyed
Popis výsledku v původním jazyce
This paper evaluates the influence of different amounts of antimony addition on the corrosion resistance of the alloy Al-Si. In the introduction of the paper is described corrosion of aluminium alloys, methods of testing and evaluation of corrosion and the influence of antimony in alloying of Al-Si alloys. For the experiment was chosen alloy Al-Si specifically AlSi7Mg0.3 alloyed by 0, 0.001, 0.005, 0.01 and 0.05 wt. % of antimony. The prepared alloys were subjected to the two types of corrosion tests inthe environment - atmosphere and corrosion chamber. The corrosion attack of experimental samples was evaluated from both the macroscopic and the microscopic point of view. The aim of this paper is to assess the influence of antimony on the corrosion resistance of the alloy AlSi7Mg0.3 which was alloyed with different amount of antimony and compared to the alloy without alloying.
Název v anglickém jazyce
Research of Corrosion Properties of Al-Si Alloys Antimony Alloyed
Popis výsledku anglicky
This paper evaluates the influence of different amounts of antimony addition on the corrosion resistance of the alloy Al-Si. In the introduction of the paper is described corrosion of aluminium alloys, methods of testing and evaluation of corrosion and the influence of antimony in alloying of Al-Si alloys. For the experiment was chosen alloy Al-Si specifically AlSi7Mg0.3 alloyed by 0, 0.001, 0.005, 0.01 and 0.05 wt. % of antimony. The prepared alloys were subjected to the two types of corrosion tests inthe environment - atmosphere and corrosion chamber. The corrosion attack of experimental samples was evaluated from both the macroscopic and the microscopic point of view. The aim of this paper is to assess the influence of antimony on the corrosion resistance of the alloy AlSi7Mg0.3 which was alloyed with different amount of antimony and compared to the alloy without alloying.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JK - Koroze a povrchové úpravy materiálu
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
N - Vyzkumna aktivita podporovana z neverejnych zdroju
Ostatní
Rok uplatnění
2013
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Manufacturing Technology
ISSN
1213-2489
e-ISSN
—
Svazek periodika
13
Číslo periodika v rámci svazku
3
Stát vydavatele periodika
CZ - Česká republika
Počet stran výsledku
6
Strana od-do
404-409
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—