Method of coating metal formes from Al-Mg and Al-Si alloys for manufacturing automobile tires

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F44555601%3A13420%2F17%3A43893661" target="_blank" >RIV/44555601:13420/17:43893661 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

ruština

Název v původním jazyce

Sposob pokrytija metallicheskikh form iz splavov tipa Al-Mg i Al-Si dlja proizvodstva avtomobilnykh shin

Popis výsledku v původním jazyce

Izobretenie otnositsja k sposobu pokrytija metallicheskikh form iz splavov dlja proizvodstva shin transportnykh sredstv tipa Al-Mg i Al-Si. V sposobe formu obezzhirivajut i protravlivajut v vanne s rN ot 11,0 do 12,5 pri temperature ot 50 do 70°S v techenie 1-2 min, promyvajut v demineralizovannojj vode pri temperature ot 20 do 30°S, zatem pogruzhajut v vannu s zhidkim cirkonievym passivirujushhim sredstvom s rN ot 4,8 do 5,2 pri temperature ot 25 do 30°S na 2-3 min, zatem vnov promyvajut v demineralizovannojj vode pri temperature ot 20 do 30°S, sushat pri temperature ot 110 do 115°S v techenie 20-25 min. Dalee formirujut okonchatelnoe pokrytie v vanne s vodnojj dispersiejj politetraftorehtilena s rN ot 7,5 do 8,5 pri temperature ot 60 do 65°S na protjazhenii 15-16 min, pokrytie obzhigajut pri temperature ot 100 do 105°S na protjazhenii 30-40 min. Izobretenie obespechivaet uvelichenie chisla ciklov izgotovlenija shin bez neobkhodimosti ochistki rabochejj poverkhnosti upomjanutojj formy dlja proizvodstva shin. 3 z.p. f-ly, 3 il.

Název v anglickém jazyce

Method of coating metal formes from Al-Mg and Al-Si alloys for manufacturing automobile tires

Popis výsledku anglicky

In the method, the form is degreased and etched in a bath with a pH from 11.0 to 12.5 at a temperature of 50 to 70°C for 1-2 minutes, washed in demineralized water at a temperature from 20 to 30°C, then it is immersed in a bath with a liquid zirconium passivating thing with a pH from 4.8 to 5.2 at a temperature of 25 to 30°C for 2-3 minutes, then again washed in demineralized water at a temperature from 20 to 30°C, dried at a temperature from 110 to115°C for 20-25 minutes. Next, a final coating is formed in the bath with an aqueous dispersion of polytetrafluoroethylene with a pH from 7.5 to 8.5 at a temperature from 60 to 65°C for 15-16 minutes, the coating is baked at a temperature from 100 to 105°C for 30-40 minutes. EFFECT: increased number of cycles of tire manufacturing without the need to clean the working surface of the mentioned form for tire manufacturing. 4 cl, 3 dwg

Druh

P - Patent

CEP obor

—

OECD FORD obor

20506 - Coating and films

Projekt

—

Návaznosti

V - Vyzkumna aktivita podporovana z jinych verejnych zdroju

Rok uplatnění

2017

Kód důvěrnosti údajů

C - Předmět řešení projektu podléhá obchodnímu tajemství (§ 504 Občanského zákoníku), ale název projektu, cíle projektu a u ukončeného nebo zastaveného projektu zhodnocení výsledku řešení projektu (údaje P03, P04, P15, P19, P29, PN8) dodané do CEP, jsou upraveny tak, aby byly zveřejnitelné.

Číslo patentu nebo vzoru

2638482

Vydavatel

RU001 -

Název vydavatele

Federal Service for Intellectual Property, Patents and Trademarks (ROSPATENT)

Místo vydání

Moscow

Stát vydání

RU - Ruská federace

Datum přijetí

13. 12. 2017

Název vlastníka

Univerzita Jana Evangelisty Purkyně v Ústí nad labem

Způsob využití

A - Výsledek využívá pouze poskytovatel

Druh možnosti využití

A - K využití výsledku jiným subjektem je vždy nutné nabytí licence