High-Temperature Processing and Recovery of Cu Catalyst Promoter
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F44555601%3A13420%2F18%3A43894198" target="_blank" >RIV/44555601:13420/18:43894198 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/61989100:27360/18:10241003
Výsledek na webu
<a href="http://dx.doi.org/10.21062/ujep/47.2018/a/1213-2489/MT/18/1/22" target="_blank" >http://dx.doi.org/10.21062/ujep/47.2018/a/1213-2489/MT/18/1/22</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.21062/ujep/47.2018/a/1213-2489/MT/18/1/22" target="_blank" >10.21062/ujep/47.2018/a/1213-2489/MT/18/1/22</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
High-Temperature Processing and Recovery of Cu Catalyst Promoter
Popis výsledku v původním jazyce
The article describes the results obtained from the plasma smelting reduction of a particular type of waste - catalyst with a Cu promoter. The catalyst is used for the process of a selective reduction of nitrobenzene (C6H5NO2) to aniline (C6H5NH2). The plasma smelting occurs in a reducing atmosphere. Six samples of the exhausted catalyst with a Cu promoter were used in the smelting process. The chemical composition of the promoter exhibited a presence of a wide range of elements. Fluorspar (fluorite) and calcium oxide (quicklime) were used as the slag-agent for the given testing. Reducing agent was the powdery graphite - waste from the manufacture of the graphite semi-finished product. The results of experiments, carried out at 80 kVA in the plasma reactor, proved that this type of catalyst can be, in fact, disposed of using the plasma technology. Recyclability of the metal contained in this waste is high; Cu ranges around 88%. Moreover, the article describes the chemical analysis of the slag, fly ash and the composition of synthesis gas in all samples of the processed catalyst.
Název v anglickém jazyce
High-Temperature Processing and Recovery of Cu Catalyst Promoter
Popis výsledku anglicky
The article describes the results obtained from the plasma smelting reduction of a particular type of waste - catalyst with a Cu promoter. The catalyst is used for the process of a selective reduction of nitrobenzene (C6H5NO2) to aniline (C6H5NH2). The plasma smelting occurs in a reducing atmosphere. Six samples of the exhausted catalyst with a Cu promoter were used in the smelting process. The chemical composition of the promoter exhibited a presence of a wide range of elements. Fluorspar (fluorite) and calcium oxide (quicklime) were used as the slag-agent for the given testing. Reducing agent was the powdery graphite - waste from the manufacture of the graphite semi-finished product. The results of experiments, carried out at 80 kVA in the plasma reactor, proved that this type of catalyst can be, in fact, disposed of using the plasma technology. Recyclability of the metal contained in this waste is high; Cu ranges around 88%. Moreover, the article describes the chemical analysis of the slag, fly ash and the composition of synthesis gas in all samples of the processed catalyst.
Klasifikace
Druh
J<sub>SC</sub> - Článek v periodiku v databázi SCOPUS
CEP obor
—
OECD FORD obor
20303 - Thermodynamics
Návaznosti výsledku
Projekt
—
Návaznosti
S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2018
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Manufacturing Technology
ISSN
1213-2489
e-ISSN
—
Svazek periodika
2018
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
CZ - Česká republika
Počet stran výsledku
7
Strana od-do
22-28
Kód UT WoS článku
—
EID výsledku v databázi Scopus
2-s2.0-85049569225