Plasma Nitriding of the P/M VANADIS 6 steel

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F45807698%3A_____%2F03%3A00009347" target="_blank" >RIV/45807698:_____/03:00009347 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Plasma Nitriding of the P/M VANADIS 6 steel

Popis výsledku v původním jazyce

The P/M made VANADIS 6 cold work steel was plasma nitrided. Important surface characteristics like the microstructure, the hardness and microhardness, the nitrogen concentration depth profiles, the phase occurrence and wear behaviour were investigated. The core material consists of the MC- and M7C3- carbides, uniformly distributed in the matrix. Plasma nitriding led to the increase of both the surface hardness and the microhardness, due to the nitrogen saturation of thin near surface region. This promotes the formation of Fe4N- and Fe3N-nitrides and, at the highest processing temperature and longer time, also the CrN-phase. The occurrence of nitrogen enriched region at the surface increases the wear resistance. On the other hand, the fracture toughnessdrops down.

Název v anglickém jazyce

Plasma Nitriding of the P/M VANADIS 6 steel

Popis výsledku anglicky

The P/M made VANADIS 6 cold work steel was plasma nitrided. Important surface characteristics like the microstructure, the hardness and microhardness, the nitrogen concentration depth profiles, the phase occurrence and wear behaviour were investigated. The core material consists of the MC- and M7C3- carbides, uniformly distributed in the matrix. Plasma nitriding led to the increase of both the surface hardness and the microhardness, due to the nitrogen saturation of thin near surface region. This promotes the formation of Fe4N- and Fe3N-nitrides and, at the highest processing temperature and longer time, also the CrN-phase. The occurrence of nitrogen enriched region at the surface increases the wear resistance. On the other hand, the fracture toughnessdrops down.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F01%2F0180" target="_blank" >GA106/01/0180: Mechanismus a kinetika sycení multifázové Fe - C - Cr - V oceli dusíkem</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2003

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Powder Metallurgy Progress

ISSN

1335 ? 8987

e-ISSN

—

Svazek periodika

3

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

SK - Slovenská republika

Počet stran výsledku

10

Strana od-do

10-19

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—