Thermal behaviour of TiO2-xNx nanostructured powder

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46356088%3A_____%2F08%3A%230000859" target="_blank" >RIV/46356088:_____/08:#0000859 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Thermal behaviour of TiO2-xNx nanostructured powder
Popis výsledku v původním jazyce
Diffusion structural analysis, based on the measurement of the release of radon previously incorporated into the samples, was used to characterize thermal behavior of N-doped titania powder prepared by heat treatment of anatase in gaseous ammonia at 575°C and the reference TiO2 powder prepared from the ST-01 anatase titania powder (Ishihara Ltd., Japan). The results of DSA, surface area and porosity measurements by nitrogen adsorption, SEM micrographs, XPS, and XRD are presented and discussed.
Název v anglickém jazyce
Thermal behaviour of TiO2-xNx nanostructured powder
Popis výsledku anglicky
Diffusion structural analysis, based on the measurement of the release of radon previously incorporated into the samples, was used to characterize thermal behavior of N-doped titania powder prepared by heat treatment of anatase in gaseous ammonia at 575°C and the reference TiO2 powder prepared from the ST-01 anatase titania powder (Ishihara Ltd., Japan). The results of DSA, surface area and porosity measurements by nitrogen adsorption, SEM micrographs, XPS, and XRD are presented and discussed.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CA - Anorganická chemie
OECD FORD obor
—

Projekt
<a href="/cs/project/LA%20292" target="_blank" >LA 292: Členství ve výboru ESTAC</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění
2008
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)