Experimental Investigation and Thermodynamic Simulation of the Uranium Oxide - Zirconium Oxide - Iron Oxide in Air

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46356088%3A_____%2F11%3A%230001022" target="_blank" >RIV/46356088:_____/11:#0001022 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Experimental Investigation and Thermodynamic Simulation of the Uranium Oxide - Zirconium Oxide - Iron Oxide in Air

Popis výsledku v původním jazyce

Melts in the UO2?UO3?ZrO2?FeO1.33?FeO1.5 system in air behave as two-phase liquids when the uranium oxide content is lower than 50 wt % and the iron oxide content is higher than 25 wt %. Melts in the UO2?UO3?ZrO2?FeO1.33?FeO1.5 system at an uranium oxidecontent lower than 50 wt % and an iron oxide content higher than 25 wt % actively exchange oxygen with atmosphere. The content of dissolved oxygen increases with a decrease in the temperature and reaches 2 wt % at 1400 °C. After the crystallization of the melt, dissolved oxygen leads to the formation of oxides containing uranium in an oxidation state of +6: UO2.2, UO2.66, and FeUO4 (see also [12]). Ingots prepared from two-phase melts in the UO2?UO3?ZrO2?FeO1.33?FeO1.5 system consist of isometric grains with structures of uranite, tetragonal modification of the zirconium oxide, and magnetite, which are separated by regions of two eutectics that differ in the composition and morphology of crystals.

Název v anglickém jazyce

Experimental Investigation and Thermodynamic Simulation of the Uranium Oxide - Zirconium Oxide - Iron Oxide in Air

Popis výsledku anglicky

Melts in the UO2?UO3?ZrO2?FeO1.33?FeO1.5 system in air behave as two-phase liquids when the uranium oxide content is lower than 50 wt % and the iron oxide content is higher than 25 wt %. Melts in the UO2?UO3?ZrO2?FeO1.33?FeO1.5 system at an uranium oxidecontent lower than 50 wt % and an iron oxide content higher than 25 wt % actively exchange oxygen with atmosphere. The content of dissolved oxygen increases with a decrease in the temperature and reaches 2 wt % at 1400 °C. After the crystallization of the melt, dissolved oxygen leads to the formation of oxides containing uranium in an oxidation state of +6: UO2.2, UO2.66, and FeUO4 (see also [12]). Ingots prepared from two-phase melts in the UO2?UO3?ZrO2?FeO1.33?FeO1.5 system consist of isometric grains with structures of uranite, tetragonal modification of the zirconium oxide, and magnetite, which are separated by regions of two eutectics that differ in the composition and morphology of crystals.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CF - Fyzikální chemie a teoretická chemie

OECD FORD obor

—

Projekt

<a href="/cs/project/ME%20944" target="_blank" >ME 944: Sledování fyzikálně-chemických vlastností systému oxidických tavenin na bázi CORIA za extrémně vysokých teplot modelujících nestandardní stavy jaderných reaktorů typu VVER</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Glass Physics and Chemistry

ISSN

1087-6596

e-ISSN

—

Svazek periodika

37

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

18

Strana od-do

—

Kód UT WoS článku

000290043000013

EID výsledku v databázi Scopus

—