Electrochemistry of samarium in lithium-beryllium fluoride salt mixture

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46356088%3A_____%2F11%3A%230001130" target="_blank" >RIV/46356088:_____/11:#0001130 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1016/S1002-0721(10)60545-5" target="_blank" >http://dx.doi.org/10.1016/S1002-0721(10)60545-5</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/S1002-0721(10)60545-5" target="_blank" >10.1016/S1002-0721(10)60545-5</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Electrochemistry of samarium in lithium-beryllium fluoride salt mixture

Popis výsledku v původním jazyce

The electrochemical behaviour of samarium was investigated in LiF-BeF2 system on an inert (Mo) electrode by cyclic voltammetry and chronopotentiometry at 804, 833, 847 and 872 K. Redox process Sm3++e-Sm2+ was recognized and analysed. Cyclic voltammetry data suggested that at potential sweep rates lower than 0,25 V/s, the reduction was limited by the diffusion of Sm3+ ions. It was not possible to observe reduction process of Sm2++2e-Sm0 due to insufficient electrochemical stability of LiF-BeF2. Diffusioncoefficients of Sm3+ ions in LiF-BeF2 were calculated from voltammetric and chronopotentiometric data in the temperature range 804-872 K. Diffusion coefficient values obeyed Arrhenius law. Activation energy was calculated to be 102,5 kJ/mol.

Název v anglickém jazyce

Electrochemistry of samarium in lithium-beryllium fluoride salt mixture

Popis výsledku anglicky

The electrochemical behaviour of samarium was investigated in LiF-BeF2 system on an inert (Mo) electrode by cyclic voltammetry and chronopotentiometry at 804, 833, 847 and 872 K. Redox process Sm3++e-Sm2+ was recognized and analysed. Cyclic voltammetry data suggested that at potential sweep rates lower than 0,25 V/s, the reduction was limited by the diffusion of Sm3+ ions. It was not possible to observe reduction process of Sm2++2e-Sm0 due to insufficient electrochemical stability of LiF-BeF2. Diffusioncoefficients of Sm3+ ions in LiF-BeF2 were calculated from voltammetric and chronopotentiometric data in the temperature range 804-872 K. Diffusion coefficient values obeyed Arrhenius law. Activation energy was calculated to be 102,5 kJ/mol.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JF - Jaderná energetika

OECD FORD obor

—

Projekt

<a href="/cs/project/2A-1TP1%2F030" target="_blank" >2A-1TP1/030: Fluoridové přepracování paliva jaderných reaktorů 4. Generace.</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Rare Earths

ISSN

1002-0721

e-ISSN

—

Svazek periodika

29

Číslo periodika v rámci svazku

8

Stát vydavatele periodika

CN - Čínská lidová republika

Počet stran výsledku

6

Strana od-do

798-803

Kód UT WoS článku

000295791300017

EID výsledku v databázi Scopus

—