Optimization of magnetic testing of ferromagnetic materials by inspection

Popis výsledku v původním jazyce

Results will be presented of magnetic testing of structural variation of low-alloyed construction steels (CSN 14260 [54SiCr6], and/or CSN 12050 [C45]), performed on a series of flat magnetically open samples, and at the same time confronted with the magntic outcome on an equivalent series of window-shaped and/or ring-shaped magnetically closed samples. The structural variation was achieved by thermal processing. All samples were first quenched from 8400C down to 200C in oil, and then individual samplesere tempered for 30 minutes at temperatures from 3000C up to 7800C. This process varied the steel structure from needle-like brittle highly-distorted martensite (quenched sample) over mixtures of partially relaxed martensite and sorbite to pure sorbite isamples tempered at the top applied temperatures. Magnetic induction measurements on the open samples were performed by U-shaped head with the magnetizing- and the pick-up-coils wound on its body.

Název v anglickém jazyce

Optimization of magnetic testing of ferromagnetic materials by inspection

Popis výsledku anglicky

Results will be presented of magnetic testing of structural variation of low-alloyed construction steels (CSN 14260 [54SiCr6], and/or CSN 12050 [C45]), performed on a series of flat magnetically open samples, and at the same time confronted with the magntic outcome on an equivalent series of window-shaped and/or ring-shaped magnetically closed samples. The structural variation was achieved by thermal processing. All samples were first quenched from 8400C down to 200C in oil, and then individual samplesere tempered for 30 minutes at temperatures from 3000C up to 7800C. This process varied the steel structure from needle-like brittle highly-distorted martensite (quenched sample) over mixtures of partially relaxed martensite and sorbite to pure sorbite isamples tempered at the top applied temperatures. Magnetic induction measurements on the open samples were performed by U-shaped head with the magnetizing- and the pick-up-coils wound on its body.

Druh

D - Stať ve sborníku

CEP obor

JS - Řízení spolehlivosti a kvality, zkušebnictví

OECD FORD obor

—

Projekt

<a href="/cs/project/GA101%2F02%2F0236" target="_blank" >GA101/02/0236: Aplikace a rozšíření preisachovské nedestruktivní magnetické metody testování konstrukčních materiálů</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

New Trends in Physics - NTF 2004. Brno

ISBN

80-214-2749-3

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

269-276

Název nakladatele

University of Technology

Místo vydání

Brno, Česká republika

Místo konání akce

Brno, Česká republika

Datum konání akce

1. 1. 2004

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—