Effect of test conditions on the bending strength of a geopolymer-reinforced composite

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24210%2F10%3A%230001606" target="_blank" >RIV/46747885:24210/10:#0001606 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Effect of test conditions on the bending strength of a geopolymer-reinforced composite

Popis výsledku v původním jazyce

This paper presents the results obtained for the effects of the loading rate and of the testing temperature on the mechanical properties, particularly on the stiffness and on the ultimate tensile strength, of a geopolymer reinforced with glass or carbonfibres. HIGH-SILICA geopolymer powder from CLUZ- CYECH and two reinforcement fibres (glass fibres-type AR and carbon fibre - HTS 5631) were used. The displacement rate is varied from 0.02 until to 2 mm/s and the testing temperature is increased from theroom temperature until the temperature of 300 A degrees C. For the case of geopolymers reinforced with carbon fibres and glass fibres, the increase of the displacement rate from 0.002 to 2 mm/s led to an improvement on the ultimate flexure strength of about 33 and 31%, respectively.

Název v anglickém jazyce

Effect of test conditions on the bending strength of a geopolymer-reinforced composite

Popis výsledku anglicky

This paper presents the results obtained for the effects of the loading rate and of the testing temperature on the mechanical properties, particularly on the stiffness and on the ultimate tensile strength, of a geopolymer reinforced with glass or carbonfibres. HIGH-SILICA geopolymer powder from CLUZ- CYECH and two reinforcement fibres (glass fibres-type AR and carbon fibre - HTS 5631) were used. The displacement rate is varied from 0.02 until to 2 mm/s and the testing temperature is increased from theroom temperature until the temperature of 300 A degrees C. For the case of geopolymers reinforced with carbon fibres and glass fibres, the increase of the displacement rate from 0.002 to 2 mm/s led to an improvement on the ultimate flexure strength of about 33 and 31%, respectively.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/FT-TA4%2F068" target="_blank" >FT-TA4/068: *Pokročilé vyztužené geopolymerní kompozity pro technické využití.</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Materials Science

ISSN

0022-2461

e-ISSN

—

Svazek periodika

454

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

5

Strana od-do

—

Kód UT WoS článku

000273033700022

EID výsledku v databázi Scopus

—