Hot rolling and deformation behavior of Fe17Al4C0.3Zr alloy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24210%2F10%3A%230001616" target="_blank" >RIV/46747885:24210/10:#0001616 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Hot rolling and deformation behavior of Fe17Al4C0.3Zr alloy

Popis výsledku v původním jazyce

The effect of the finish rolling temperature on the deformation resistance and microstructure of a cast ferrite with a high content of aluminum and particles was investigated in the temperature range of 1089 to 1406 K. The recrystallized structure of theFe17Al4Cr0.3Zr at. % alloy was achieved, either during the hot rolling and subsequent cooling or during the recrystallization annealing after the cold rolling. The deformation behavior, as well as the softening processes, are connected with movement ofthe grain boundaries through the array of (Fe,Al)(2)Zr particles and by the interaction of dislocations with ZrC particles. It was approved that the deformation resistance of various Fe-Al alloys with different aluminum contents are similar at high temperatures. The grain size of the initial casting was refined by the applied hot rolling process by approximately one order. The annealing at 1173 K was sufficient to start the static recrystallization in the cold rolled material.

Název v anglickém jazyce

Hot rolling and deformation behavior of Fe17Al4C0.3Zr alloy

Popis výsledku anglicky

The effect of the finish rolling temperature on the deformation resistance and microstructure of a cast ferrite with a high content of aluminum and particles was investigated in the temperature range of 1089 to 1406 K. The recrystallized structure of theFe17Al4Cr0.3Zr at. % alloy was achieved, either during the hot rolling and subsequent cooling or during the recrystallization annealing after the cold rolling. The deformation behavior, as well as the softening processes, are connected with movement ofthe grain boundaries through the array of (Fe,Al)(2)Zr particles and by the interaction of dislocations with ZrC particles. It was approved that the deformation resistance of various Fe-Al alloys with different aluminum contents are similar at high temperatures. The grain size of the initial casting was refined by the applied hot rolling process by approximately one order. The annealing at 1173 K was sufficient to start the static recrystallization in the cold rolled material.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

High temperature materials and processes

ISSN

0334-6455

e-ISSN

—

Svazek periodika

29

Číslo periodika v rámci svazku

1-2

Stát vydavatele periodika

IL - Stát Izrael

Počet stran výsledku

7

Strana od-do

—

Kód UT WoS článku

000280351300002

EID výsledku v databázi Scopus

—