Modelling of magnetoelastic coupling in COMSOL Multiphysics

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24210%2F12%3A%230002747" target="_blank" >RIV/46747885:24210/12:#0002747 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Modelling of magnetoelastic coupling in COMSOL Multiphysics

Popis výsledku v původním jazyce

Magnetorheological elastomers (MREs), also referred to as magnetosensitive (MS) elastomers, are smart materials composed of micron-sized ferrous particles dispersed in a polymer matrix. Commonly, magnetic fields are applied to the polymer composite during cross-linking so that chainlike columnar particle structures can be formed and fixed in the matrix after curing. The unique characteristic of MRE is that its shear modulus can be continuously controlled by the external magnetic field. Shearing of the cured composite in the presence of the magnetic field causes particle displacement from their low energy state, thereby requiring additional work. This work rises monotonically with applied magnetic field, thus resulting in a field dependent shear modulus.

Název v anglickém jazyce

Modelling of magnetoelastic coupling in COMSOL Multiphysics

Popis výsledku anglicky

Magnetorheological elastomers (MREs), also referred to as magnetosensitive (MS) elastomers, are smart materials composed of micron-sized ferrous particles dispersed in a polymer matrix. Commonly, magnetic fields are applied to the polymer composite during cross-linking so that chainlike columnar particle structures can be formed and fixed in the matrix after curing. The unique characteristic of MRE is that its shear modulus can be continuously controlled by the external magnetic field. Shearing of the cured composite in the presence of the magnetic field causes particle displacement from their low energy state, thereby requiring additional work. This work rises monotonically with applied magnetic field, thus resulting in a field dependent shear modulus.

Druh

D - Stať ve sborníku

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GAP108%2F10%2F1296" target="_blank" >GAP108/10/1296: Vývoj a charakterizace aktivních hybridních textilií s integrovanými NiTi vlákny mikronových průměrů s nanozrnnou strukturou</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

COMPUTATIONAL MECHANICS 2012 EXTENDED ABSTRACTS

ISBN

978-80-261-0157-4

ISSN

—

e-ISSN

—

Počet stran výsledku

2

Strana od-do

—

Název nakladatele

University of West Bohemia, Pilsen

Místo vydání

Plzeň

Místo konání akce

Plzeň

Datum konání akce

1. 1. 2012

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—