Corrosion resistance of heat-resistance alloys in molten lead crystal at 1200°C
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24210%2F12%3A%230002779" target="_blank" >RIV/46747885:24210/12:#0002779 - isvavai.cz</a>
Výsledek na webu
<a href="http://www.metal2013.com/files/proceedings/02/reports/435.pdf" target="_blank" >http://www.metal2013.com/files/proceedings/02/reports/435.pdf</a>
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Corrosion resistance of heat-resistance alloys in molten lead crystal at 1200°C
Popis výsledku v původním jazyce
The important parameter for using heat-resistance alloys in the glass industry is the corrosion resistance of alloys in molten glass. The corrosion resistance of the alloy depends on the chemical composition of the glass and alloy and the temperature. The corrosion tests of iron aluminide Fe14Al5Cr, austenitic steel EN X8CrNi25-21 and nickel alloy were carried out in a lead crystal at 1200°C. The corrosion kinetic of the test alloys was determined by the measurement of weight loss. The changes of samplesurface layers were quantified by the surface roughness. The most suitable alloy for application in molten lead crystal is the iron aluminide Fe14Al5Cr. The alloy Fe14Al5Cr has had the lowest weight loss and parameters of roughness, tinted the molten glass at the least. The corrosion resistance of the austenitic steel against the molten lead crystal is also very good.
Název v anglickém jazyce
Corrosion resistance of heat-resistance alloys in molten lead crystal at 1200°C
Popis výsledku anglicky
The important parameter for using heat-resistance alloys in the glass industry is the corrosion resistance of alloys in molten glass. The corrosion resistance of the alloy depends on the chemical composition of the glass and alloy and the temperature. The corrosion tests of iron aluminide Fe14Al5Cr, austenitic steel EN X8CrNi25-21 and nickel alloy were carried out in a lead crystal at 1200°C. The corrosion kinetic of the test alloys was determined by the measurement of weight loss. The changes of samplesurface layers were quantified by the surface roughness. The most suitable alloy for application in molten lead crystal is the iron aluminide Fe14Al5Cr. The alloy Fe14Al5Cr has had the lowest weight loss and parameters of roughness, tinted the molten glass at the least. The corrosion resistance of the austenitic steel against the molten lead crystal is also very good.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2012
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
METAL 2012
ISBN
978-80-87294-31-4
ISSN
—
e-ISSN
—
Počet stran výsledku
5
Strana od-do
1467-1471
Název nakladatele
Tanger, s.r.o.
Místo vydání
Ostrava
Místo konání akce
Brno
Datum konání akce
1. 1. 2012
Typ akce podle státní příslušnosti
CST - Celostátní akce
Kód UT WoS článku
—