The effect of Zr on high-temperature oxidation behaviour of Fe3Al-based alloys
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24210%2F15%3A00001952" target="_blank" >RIV/46747885:24210/15:00001952 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/25797000:_____/15:#0000572
Výsledek na webu
<a href="http://www.sciencedirect.com/science/article/pii/S0010938X15300135" target="_blank" >http://www.sciencedirect.com/science/article/pii/S0010938X15300135</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.corsci.2015.07.016" target="_blank" >10.1016/j.corsci.2015.07.016</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
The effect of Zr on high-temperature oxidation behaviour of Fe3Al-based alloys
Popis výsledku v původním jazyce
The cyclic oxidation of Fe-30Al-xZr and Fe-25Al-xZr (x=0.3-5.2 at.%) has been investigated at 900 degrees C and 1100 degrees C in laboratory air. Scales, oxide protrusions and structural changes were analysed by LOM, XRD, SEM and EDS. The oxidation rateincreases with increasing Zr content as well as with increasing temperature. Spallation of thin scales formed at 900 degrees C on the Zr lean alloys is observed, while thicker scales formed on Zr-rich alloys or at 1100 degrees C show cracking but do notspall. At both temperatures the scales on all alloys consist of Al2O3, Fe2O3 and ZrO2 and oxide protrusions penetrate into the samples. These protrusions form by preferential oxidation of Zr rich phases. (C) 2015 Elsevier Ltd. All rights reserved.
Název v anglickém jazyce
The effect of Zr on high-temperature oxidation behaviour of Fe3Al-based alloys
Popis výsledku anglicky
The cyclic oxidation of Fe-30Al-xZr and Fe-25Al-xZr (x=0.3-5.2 at.%) has been investigated at 900 degrees C and 1100 degrees C in laboratory air. Scales, oxide protrusions and structural changes were analysed by LOM, XRD, SEM and EDS. The oxidation rateincreases with increasing Zr content as well as with increasing temperature. Spallation of thin scales formed at 900 degrees C on the Zr lean alloys is observed, while thicker scales formed on Zr-rich alloys or at 1100 degrees C show cracking but do notspall. At both temperatures the scales on all alloys consist of Al2O3, Fe2O3 and ZrO2 and oxide protrusions penetrate into the samples. These protrusions form by preferential oxidation of Zr rich phases. (C) 2015 Elsevier Ltd. All rights reserved.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JK - Koroze a povrchové úpravy materiálu
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GAP108%2F12%2F1452" target="_blank" >GAP108/12/1452: Optimalizace vysokoteplotních mechanických vlastností aluminidů železa typu Fe3Al s karbidotvornými prvky</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Corrosion Science
ISSN
0010-938X
e-ISSN
—
Svazek periodika
100
Číslo periodika v rámci svazku
November 2015
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
11
Strana od-do
147-157
Kód UT WoS článku
000363070100013
EID výsledku v databázi Scopus
—