Fractal geometry used for evaluation of corrosion resistance of Fe-14Al-6Cr wt.% against molten glass

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24210%2F15%3A00002462" target="_blank" >RIV/46747885:24210/15:00002462 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Fractal geometry used for evaluation of corrosion resistance of Fe-14Al-6Cr wt.% against molten glass

Popis výsledku v původním jazyce

Corrosive attack of metals and alloys by molten glass can be described by parameters of surface roughness. Fractal geometry and statistic tools were used for surface roughness quantification. The obtained parameters of fractal geometry and statistics were determined on boundary curves between alloys and glass which had been generated from the digital photography of sample cross-section. This methodology was successfully used for quantification of surface changes of iron aluminides Fe-14Al-6Cr and austenitic steel during corrosion test in molten soda-lime glass at 1200°C.

Název v anglickém jazyce

Fractal geometry used for evaluation of corrosion resistance of Fe-14Al-6Cr wt.% against molten glass

Popis výsledku anglicky

Corrosive attack of metals and alloys by molten glass can be described by parameters of surface roughness. Fractal geometry and statistic tools were used for surface roughness quantification. The obtained parameters of fractal geometry and statistics were determined on boundary curves between alloys and glass which had been generated from the digital photography of sample cross-section. This methodology was successfully used for quantification of surface changes of iron aluminides Fe-14Al-6Cr and austenitic steel during corrosion test in molten soda-lime glass at 1200°C.

Druh

J_SC - Článek v periodiku v databázi SCOPUS

CEP obor

—

OECD FORD obor

20506 - Coating and films

Projekt

<a href="/cs/project/GAP108%2F12%2F1452" target="_blank" >GAP108/12/1452: Optimalizace vysokoteplotních mechanických vlastností aluminidů železa typu Fe3Al s karbidotvornými prvky</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Manufacturing Technology

ISSN

1213-2489

e-ISSN

—

Svazek periodika

15

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

8

Strana od-do

534-541

Kód UT WoS článku

—

EID výsledku v databázi Scopus

2-s2.0-84949204559