Cathodic Arc Deposition of TiCN Coatings - Influence of the C2H2/N2 Ratio on the Structure and Coating Properties
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24210%2F18%3A00005128" target="_blank" >RIV/46747885:24210/18:00005128 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/46747885:24620/18:00005128 RIV/44555601:13440/18:43893959
Výsledek na webu
<a href="https://www.scientific.net/JNanoR.51.78" target="_blank" >https://www.scientific.net/JNanoR.51.78</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/JNanoR.51.78" target="_blank" >10.4028/www.scientific.net/JNanoR.51.78</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Cathodic Arc Deposition of TiCN Coatings - Influence of the C2H2/N2 Ratio on the Structure and Coating Properties
Popis výsledku v původním jazyce
TiCN thin coatings with various different carbon contents were deposited using cathode arc evaporation of pure titanium in a mixture of N2 and C2H2 gasses at a constant pressure of 1.5 Pa. The analyses show a transition from a stoichiometric to a non-stoichiometric coating structure with an increasing C2H2 content. Moreover, the increase in the acetylene in the gas mixture leads to a decrease in the crystal phase from pure polycrystalline to pure amorphous. Nanohardness changes from 30.4 to 4.4 GPa and the cohesive failure of the coatings is in the range of 61 - 72 N. The tribology is estimated by the Ball-on-Disc method and an Si3N4 ball as the counterpart. The measured coefficient of friction is in the range of 0.2 - 0.56
Název v anglickém jazyce
Cathodic Arc Deposition of TiCN Coatings - Influence of the C2H2/N2 Ratio on the Structure and Coating Properties
Popis výsledku anglicky
TiCN thin coatings with various different carbon contents were deposited using cathode arc evaporation of pure titanium in a mixture of N2 and C2H2 gasses at a constant pressure of 1.5 Pa. The analyses show a transition from a stoichiometric to a non-stoichiometric coating structure with an increasing C2H2 content. Moreover, the increase in the acetylene in the gas mixture leads to a decrease in the crystal phase from pure polycrystalline to pure amorphous. Nanohardness changes from 30.4 to 4.4 GPa and the cohesive failure of the coatings is in the range of 61 - 72 N. The tribology is estimated by the Ball-on-Disc method and an Si3N4 ball as the counterpart. The measured coefficient of friction is in the range of 0.2 - 0.56
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
20506 - Coating and films
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2018
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Nano Research,
ISSN
1662-5250
e-ISSN
—
Svazek periodika
51
Číslo periodika v rámci svazku
February
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
14
Strana od-do
78-91
Kód UT WoS článku
000429502900008
EID výsledku v databázi Scopus
2-s2.0-85059404703