Local Mechanical Properties of Zinc-Iron Coated Steel Sheets by Depth- Sensing Indentation
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24210%2F18%3A00006192" target="_blank" >RIV/46747885:24210/18:00006192 - isvavai.cz</a>
Výsledek na webu
<a href="https://www.scientific.net/KEM.784.153" target="_blank" >https://www.scientific.net/KEM.784.153</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.784.153" target="_blank" >10.4028/www.scientific.net/KEM.784.153</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Local Mechanical Properties of Zinc-Iron Coated Steel Sheets by Depth- Sensing Indentation
Popis výsledku v původním jazyce
Depth-sensing indentation (DSI) is used in this work to determine the change of local mechanical properties by annealing of hot-dip galvanized IF steel sheets. The influence of annealing conditions (temperature and time) on: (i) coating composition; (ii) local mechanical properties and (iii) roughness of the coating surface was quantified. Annealing of steel samples (Ti-IF steel and Ti- Nb-P-IF steel alloyed with phosphorus) was performed with different holding times (10, 60, and 300 s) by both temperatures 450 and 550 °C. The zinc in coating transformed during annealing to the intermetallic phases ZnxFey. Annealed Zn-Fe coatings, wherein the iron concentration falls towards the surface, consist of different intermetallic phases.
Název v anglickém jazyce
Local Mechanical Properties of Zinc-Iron Coated Steel Sheets by Depth- Sensing Indentation
Popis výsledku anglicky
Depth-sensing indentation (DSI) is used in this work to determine the change of local mechanical properties by annealing of hot-dip galvanized IF steel sheets. The influence of annealing conditions (temperature and time) on: (i) coating composition; (ii) local mechanical properties and (iii) roughness of the coating surface was quantified. Annealing of steel samples (Ti-IF steel and Ti- Nb-P-IF steel alloyed with phosphorus) was performed with different holding times (10, 60, and 300 s) by both temperatures 450 and 550 °C. The zinc in coating transformed during annealing to the intermetallic phases ZnxFey. Annealed Zn-Fe coatings, wherein the iron concentration falls towards the surface, consist of different intermetallic phases.
Klasifikace
Druh
J<sub>ost</sub> - Ostatní články v recenzovaných periodicích
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
—
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2018
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Key Engineering Materials
ISSN
1662-9795
e-ISSN
—
Svazek periodika
784
Číslo periodika v rámci svazku
neuvedeno
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
6
Strana od-do
153-158
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—