Failure of glass fibre-reinforced polypropylene metal laminate subjected to close-range explosion

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24210%2F20%3A00007889" target="_blank" >RIV/46747885:24210/20:00007889 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/46747885:24620/20:00007889

Výsledek na webu

<a href="https://www.mdpi.com/2073-4360/12/9/2139" target="_blank" >https://www.mdpi.com/2073-4360/12/9/2139</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.3390/polym12092139" target="_blank" >10.3390/polym12092139</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Failure of glass fibre-reinforced polypropylene metal laminate subjected to close-range explosion

Popis výsledku v původním jazyce

The present study investigates the effects of close-range blast loading of fibre metal laminates (FMLs) fabricated from woven glass polypropylene and aluminium alloy 2024-T3. The polypropylene layers and anodized aluminium are stacked in 3/2 layering configuration to investigate the impact energy absorbed through deformation and damage. In order to study the blast responses of FMLs, a 4-cable instrumented pendulum blast set-up is used. Effects of blast impulse and stand-off distance were examined. Investigation of the cross-section of FMLs are presented and damages such as fibre fracture, debonding, and global deformation are examined. Increasing stand-off distance from 4 to 14 mm resulted in a change of damage mode from highly localized perforation to global deformation.

Název v anglickém jazyce

Failure of glass fibre-reinforced polypropylene metal laminate subjected to close-range explosion

Popis výsledku anglicky

The present study investigates the effects of close-range blast loading of fibre metal laminates (FMLs) fabricated from woven glass polypropylene and aluminium alloy 2024-T3. The polypropylene layers and anodized aluminium are stacked in 3/2 layering configuration to investigate the impact energy absorbed through deformation and damage. In order to study the blast responses of FMLs, a 4-cable instrumented pendulum blast set-up is used. Effects of blast impulse and stand-off distance were examined. Investigation of the cross-section of FMLs are presented and damages such as fibre fracture, debonding, and global deformation are examined. Increasing stand-off distance from 4 to 14 mm resulted in a change of damage mode from highly localized perforation to global deformation.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

10404 - Polymer science

Projekt

<a href="/cs/project/EF16_025%2F0007293" target="_blank" >EF16_025/0007293: Modulární platforma pro autonomní podvozky specializovaných elektrovozidel pro dopravu nákladu a zařízení</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2020

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Polymers

ISSN

2073-4360

e-ISSN

—

Svazek periodika

12

Číslo periodika v rámci svazku

9

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

14

Strana od-do

—

Kód UT WoS článku

000583337000001

EID výsledku v databázi Scopus

2-s2.0-85092427243