Polyurethane coating on a supporting layer of polymeric nanofibers

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24410%2F12%3A%230001205" target="_blank" >RIV/46747885:24410/12:#0001205 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Polyurethane coating on a supporting layer of polymeric nanofibers
Popis výsledku v původním jazyce
Nanoindentation creep tests in polymeric optical fibers with 1~2 cm thickness were carried out with different loading times under the maximum load 10mN and holding time 10 s. The results showed the strong loading rate sensitivity on stress exponent and hardness. The elastic modulus was decreased slightly (less than 2%) due to the creep effect remaining during the initial unloading period.
Název v anglickém jazyce
Polyurethane coating on a supporting layer of polymeric nanofibers
Popis výsledku anglicky
Nanoindentation creep tests in polymeric optical fibers with 1~2 cm thickness were carried out with different loading times under the maximum load 10mN and holding time 10 s. The results showed the strong loading rate sensitivity on stress exponent and hardness. The elastic modulus was decreased slightly (less than 2%) due to the creep effect remaining during the initial unloading period.