NANOFIBROUS VASCULAR GRAFT RELEASING NITRIC OXIDE

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24410%2F14%3A%230003929" target="_blank" >RIV/46747885:24410/14:#0003929 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
NANOFIBROUS VASCULAR GRAFT RELEASING NITRIC OXIDE
Popis výsledku v původním jazyce
Small diameter vascular grafts incorporating long term nitric oxide (NO) release were prepared by electrospinning. Nanofibrous vascular grafts made from biodegradable polymer polycaprolactone were modified by the addition of novel, NO-releasing compoundfrom the group of S-Nitrosothiols. An initial burst of NO was measured leading to long term release during 10 days at 37°C measured in vitro. This demonstrates the presence of NO-releasing groups entrapped within the fibers that are believed to improve vascular graft properties.
Název v anglickém jazyce
NANOFIBROUS VASCULAR GRAFT RELEASING NITRIC OXIDE
Popis výsledku anglicky
Small diameter vascular grafts incorporating long term nitric oxide (NO) release were prepared by electrospinning. Nanofibrous vascular grafts made from biodegradable polymer polycaprolactone were modified by the addition of novel, NO-releasing compoundfrom the group of S-Nitrosothiols. An initial burst of NO was measured leading to long term release during 10 days at 37°C measured in vitro. This demonstrates the presence of NO-releasing groups entrapped within the fibers that are believed to improve vascular graft properties.

Projekt
—
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)