Needleless Electrospinning of Silk Fibroin/Gelatin Blend Nanofibres

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24410%2F14%3A%230003946" target="_blank" >RIV/46747885:24410/14:#0003946 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Needleless Electrospinning of Silk Fibroin/Gelatin Blend Nanofibres

Popis výsledku v původním jazyce

. In this study, nanofibres consisting of silk fibroin (SF) and gelatin (GP) with different composition ratio were fabricated by needleless electrospinning method. The influences of SF/GP blending ratio on the properties of spinning solution and the morphology of electrospun fibres were investigated. A variety of compositions of the silk fibroin/gelatin blend solutions were successfully electrospun into nanofibres sheet. The morphology of electrospun fibre was characterized by a scanning electron microscope (SEM) which indicates that the morphology of obtained fibres was influenced by the weight ratio of gelatin to silk fibroin in the spinning solution. It was observed that the blending ratio of gelatin to silk fibroin in spinning solution played an important role in spinning performance of the process and the diameter of obtained fibres. An increasing in gelatin content in blended solution resulted in bigger diameter of the obtained electrospun fibres. The silk fibroin/gelatin electro

Název v anglickém jazyce

Needleless Electrospinning of Silk Fibroin/Gelatin Blend Nanofibres

Popis výsledku anglicky

. In this study, nanofibres consisting of silk fibroin (SF) and gelatin (GP) with different composition ratio were fabricated by needleless electrospinning method. The influences of SF/GP blending ratio on the properties of spinning solution and the morphology of electrospun fibres were investigated. A variety of compositions of the silk fibroin/gelatin blend solutions were successfully electrospun into nanofibres sheet. The morphology of electrospun fibre was characterized by a scanning electron microscope (SEM) which indicates that the morphology of obtained fibres was influenced by the weight ratio of gelatin to silk fibroin in the spinning solution. It was observed that the blending ratio of gelatin to silk fibroin in spinning solution played an important role in spinning performance of the process and the diameter of obtained fibres. An increasing in gelatin content in blended solution resulted in bigger diameter of the obtained electrospun fibres. The silk fibroin/gelatin electro

Druh

O - Ostatní výsledky

CEP obor

CD - Makromolekulární chemie

OECD FORD obor

—

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů