Thermomechanical properties of glass fabric/epoxy composites filled with fly ash

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24410%2F15%3A00002980" target="_blank" >RIV/46747885:24410/15:00002980 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.sciencedirect.com/science/article/pii/S1359836815005934" target="_blank" >http://www.sciencedirect.com/science/article/pii/S1359836815005934</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.compositesb.2015.09.049" target="_blank" >10.1016/j.compositesb.2015.09.049</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Thermomechanical properties of glass fabric/epoxy composites filled with fly ash

Popis výsledku v původním jazyce

The mechanical activation of fly ash was carried out using ball milling to promote adhesion with epoxy. The 5 h of wet pulverization was found to result into particle size of less than 500 nm. The obtained nanoparticles were incorporated into epoxy to prepare three layered laminated composite of glass fabrics. The results revealed substantial improvement in mechanical properties of nanocomposites as compared to neat and unmilled fly ash composites. Moreover, the storage modulus exhibited 85.71, 38.09, 104.76 and 80.95% increment over neat composites for 1, 3, 5 and 10 wt% of activated fly ash at 200 degrees C.

Název v anglickém jazyce

Thermomechanical properties of glass fabric/epoxy composites filled with fly ash

Popis výsledku anglicky

The mechanical activation of fly ash was carried out using ball milling to promote adhesion with epoxy. The 5 h of wet pulverization was found to result into particle size of less than 500 nm. The obtained nanoparticles were incorporated into epoxy to prepare three layered laminated composite of glass fabrics. The results revealed substantial improvement in mechanical properties of nanocomposites as compared to neat and unmilled fly ash composites. Moreover, the storage modulus exhibited 85.71, 38.09, 104.76 and 80.95% increment over neat composites for 1, 3, 5 and 10 wt% of activated fly ash at 200 degrees C.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/EE2.3.30.0065" target="_blank" >EE2.3.30.0065: Podpora tvorby excelentních výzkumných a vývojových týmů na Technické univerzitě v Liberci</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Composites B

ISSN

1359-8368

e-ISSN

—

Svazek periodika

85

Číslo periodika v rámci svazku

3816

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

9

Strana od-do

268-276

Kód UT WoS článku

000367120500028

EID výsledku v databázi Scopus

2-s2.0-84944408389