NANOINDENTATION MEASUREMENTS OF JUTE/POLY LACTIC ACID COMPOSITES
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24410%2F15%3A00003174" target="_blank" >RIV/46747885:24410/15:00003174 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
NANOINDENTATION MEASUREMENTS OF JUTE/POLY LACTIC ACID COMPOSITES
Popis výsledku v původním jazyce
The performance of natural fiber reinforced polymer composites depends on the quality of stress transfer in the interphase between fiber and polymer in the composite. However, due to the difficulty in measurement of mechanical properties at interphase, the composites show uncertain trend in improvement of performance. The purpose of this study was to measure the mechanical properties of the interphase using nanoindentation technique. In the present study, 3 wt % of jute fibers of millimeter, micrometerand nanometer scales were incorporated in poly lactic acid (PLA) matrix to prepare composite films by solvent casting. The reinforcement potentials of fibers at different sizes from millimeter to nanometer were investigated from the improvements in elastic modulus of composite films based on nanoindentation measurements. The increase in elastic modulus was observed by 65.21 %, 25.40 % and 13.04% for composite films of nanofibers, microfibers and milifibers respectively compared to neat P
Název v anglickém jazyce
NANOINDENTATION MEASUREMENTS OF JUTE/POLY LACTIC ACID COMPOSITES
Popis výsledku anglicky
The performance of natural fiber reinforced polymer composites depends on the quality of stress transfer in the interphase between fiber and polymer in the composite. However, due to the difficulty in measurement of mechanical properties at interphase, the composites show uncertain trend in improvement of performance. The purpose of this study was to measure the mechanical properties of the interphase using nanoindentation technique. In the present study, 3 wt % of jute fibers of millimeter, micrometerand nanometer scales were incorporated in poly lactic acid (PLA) matrix to prepare composite films by solvent casting. The reinforcement potentials of fibers at different sizes from millimeter to nanometer were investigated from the improvements in elastic modulus of composite films based on nanoindentation measurements. The increase in elastic modulus was observed by 65.21 %, 25.40 % and 13.04% for composite films of nanofibers, microfibers and milifibers respectively compared to neat P
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JI - Kompositní materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Interntional conference on natural fibers
ISBN
978-989-98468-5-2
ISSN
—
e-ISSN
—
Počet stran výsledku
2
Strana od-do
49-50
Název nakladatele
ICNF2015
Místo vydání
Portugal
Místo konání akce
Azores, Portugal
Datum konání akce
1. 1. 2015
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—