SPINNABILITY OF POLY (ε – CAPROLACTONE) USING FORMIC ACID BY ALTERNATING CURRENT ELECTROSPINNING

Kód výsledku v IS VaVaI

RIV/46747885:24410/16:00003967 - isvavai.cz

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

SPINNABILITY OF POLY (ε – CAPROLACTONE) USING FORMIC ACID BY ALTERNATING CURRENT ELECTROSPINNING

Popis výsledku v původním jazyce

First time Poly (ε – caprolactone) bioabsorbable nano and micro fibers have been fabricated by uncommon Needle and collector less Alternating Current Electrospinning at the rate of 6.72 g per hour using Formic acid. Present work clearly describe the effect of solution concentration (5%, 10%, and 15%) viscosity, fiber morphology and applied voltage (20 to 38Kv) during electrospinning have been investigated. Fiber diameter is increasing with respect to polymer concentration and an applied AC voltage.

Název v anglickém jazyce

SPINNABILITY OF POLY (ε – CAPROLACTONE) USING FORMIC ACID BY ALTERNATING CURRENT ELECTROSPINNING

Popis výsledku anglicky

First time Poly (ε – caprolactone) bioabsorbable nano and micro fibers have been fabricated by uncommon Needle and collector less Alternating Current Electrospinning at the rate of 6.72 g per hour using Formic acid. Present work clearly describe the effect of solution concentration (5%, 10%, and 15%) viscosity, fiber morphology and applied voltage (20 to 38Kv) during electrospinning have been investigated. Fiber diameter is increasing with respect to polymer concentration and an applied AC voltage.

Druh

O - Ostatní výsledky

CEP obor

CE - Biochemie

OECD FORD obor

—

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů