Preparation of Coated Polyamide Nanofibrous Membranes with Phase Change Material
Popis výsledku v původním jazyce
PEG-coated PA6 nanofibrous membranes have been prepared and latent heat of fusion of all samples was approximately larger than 100J/g. The all PEG-coated PA6 nanofibrous membranes had similar phase transition process but the latent heat of fusion was affected by the content of PEG in the coated samples. The latent heat of fusion increased obviously when the content of PEG was larger than 70wt%.
Název v anglickém jazyce
Preparation of Coated Polyamide Nanofibrous Membranes with Phase Change Material
Popis výsledku anglicky
PEG-coated PA6 nanofibrous membranes have been prepared and latent heat of fusion of all samples was approximately larger than 100J/g. The all PEG-coated PA6 nanofibrous membranes had similar phase transition process but the latent heat of fusion was affected by the content of PEG in the coated samples. The latent heat of fusion increased obviously when the content of PEG was larger than 70wt%.

Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Rok uplatnění
2019
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)