Structure of Inorganic-organic Xerogels Studied by Infrared Spectroscopy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24510%2F16%3A00005150" target="_blank" >RIV/46747885:24510/16:00005150 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

slovinština

Název v původním jazyce

Štruktúra anorganicko-organických xerogélov sledovaná infračervenou spektroskopiou

Popis výsledku v původním jazyce

Práca sa zaoberá zisťovaním štruktúry anorganicko-organických xerogélov pripravených zo sólov v systéme tetraetoxysilán (TEOS) – trietoxyoktylsilán (TriEOS) – voda – kyselina dusičná – izopropanol pomocou infračervenej spektroskopie. Metódou sól-gél sa pripravili sóly, v ktorých bol mólový pomer x(TEOS):x(TriEOS) = 8:0, 7:1, 6:2, 5:3, 4:4 a mólový pomer x(H2O)/x(SiO2) = 2, 4, 6. Pripravilo sa 15 xerogélov sušením pri teplote 80 °C. V oblasti vlnočtov 1 300 – 700 cm-1 sa reflexnou technikou namerané infračervené spektrá podrobili separácii pásov. Z hodnôt integrovaných intenzít zistených zo separácie pásov sa vypočítali pomery štvor a šesťčlánkových štruktúrnych jednotiek, ako aj skupín Si-OH a Si-O-, k celkovej kremičitej sieti. Separáciou sa získali aj zložky priradené LO a TO módom pásu asymetrickej valenčnej vibrácie.

Název v anglickém jazyce

Structure of Inorganic-organic Xerogels Studied by Infrared Spectroscopy

Popis výsledku anglicky

The properties of materials are determined by a large number of processing parameters, as well as by their structure. For the study of material structure, the infrared spectroscopy is very useful technique, because reveals the energies of possible stretching vibrations within the solid network. The assignment of these vibrations to individual chemical groups allows the qualitative and quantitative characterization of the chemical components of the solid network. The paper gives a detailed description relating to the study of the structure of inorganic-organic xerogels using the infrared spectroscopy. Fifteen xerogels were prepared from sols in „tetraethoxysilane (TEOS) – octyltriethoxysilane (TriEOS) – water – nitric acid – isopropyl alcohol“ system. In sols, which were prepared by the sol-gel method, the mole ratios of x(TEOS):x(TriEOS) were 8:0, 7:1, 6:2, 5:3, 4:4 and the mole ratios of x(H2O)/x(SiO2) were 2, 4 and 6. Drying at a temperature of 80 °C was used for the preparation of inorganic-organic xerogels. The xerogels were characterized by infrared spectroscopy using reflex mode in the spectral range of 4 000 – 700 cm-1. The results show that the mole ratios of x(TEOS):x(TriEOS) and x(H2O)/x(SiO2) had the effect mainly on bands of asymmetric and symmetric C-H stretching vibrations, bending C-H vibrations, antisymmetric Si-O-Si stretching vibrations and Si-OH stretching vibrations. The fingerprint region of spectra is situated at 1 300 – 700 cm-1 and it provides information about the structure of the silica network. Band deconvolution was carried out in this spectral region using seven Gaussian curves. Deconvolution made it possible to detect four- and six-membered siloxane rings, as well as silanol groups in the structure of xerogels. The band of antisymmetric Si-O-Si stretching vibrations at 1 200 – 1 050 cm-1 was decomposed into two transversal optic and two longitudinal optic components – TO and LO modes. The band near 940 cm-1 was decomposed into two components associating with Si-OH and Si-O- groups.

Druh

J_ost - Ostatní články v recenzovaných periodicích

CEP obor

—

OECD FORD obor

10403 - Physical chemistry

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Hutnické listy

ISSN

0018-8069

e-ISSN

—

Svazek periodika

69

Číslo periodika v rámci svazku

5

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

5

Strana od-do

90-94

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—