Structure?property relationships in Sterculia urens/polyvinyl alcohol electrospun composite nanofibres

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24620%2F15%3A00001536" target="_blank" >RIV/46747885:24620/15:00001536 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.sciencedirect.com/science/article/pii/S014486171401176X" target="_blank" >http://www.sciencedirect.com/science/article/pii/S014486171401176X</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.carbpol.2014.12.002" target="_blank" >10.1016/j.carbpol.2014.12.002</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Structure?property relationships in Sterculia urens/polyvinyl alcohol electrospun composite nanofibres

Popis výsledku v původním jazyce

Sterculia urens (Gum Karaya) based polyvinyl alcohol (PVA) composite nanofibres have been successfully electrospun after chemical modification of S. urens to increase its solubility. The effect of deacetylated S. urens (DGK) on the morphology, structure,crystallization behaviour and thermal stability was studied for spuned fibres before and after spinning post treatment. An apparent increase in the PVA crystallinity were observed in the PVA?DGK composite nanofibres indicating S. urens induced crystallization of PVA. The pure PVA nanofibre and the nanofibres of PVA?DGK composites were introduced to post electrospinning heat treatment at 150 °C for 15 min. The presence of sterculia gum reduced the fibre diameter and distribution of the nanofibres due tothe increased stretching of the fibres during spinning. Switching of the thermal behaviour occurs due to post spinning heat treatments

Název v anglickém jazyce

Structure?property relationships in Sterculia urens/polyvinyl alcohol electrospun composite nanofibres

Popis výsledku anglicky

Sterculia urens (Gum Karaya) based polyvinyl alcohol (PVA) composite nanofibres have been successfully electrospun after chemical modification of S. urens to increase its solubility. The effect of deacetylated S. urens (DGK) on the morphology, structure,crystallization behaviour and thermal stability was studied for spuned fibres before and after spinning post treatment. An apparent increase in the PVA crystallinity were observed in the PVA?DGK composite nanofibres indicating S. urens induced crystallization of PVA. The pure PVA nanofibre and the nanofibres of PVA?DGK composites were introduced to post electrospinning heat treatment at 150 °C for 15 min. The presence of sterculia gum reduced the fibre diameter and distribution of the nanofibres due tothe increased stretching of the fibres during spinning. Switching of the thermal behaviour occurs due to post spinning heat treatments

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CD - Makromolekulární chemie

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Carbohydrate Polymers

ISSN

0144-8617

e-ISSN

—

Svazek periodika

120

Číslo periodika v rámci svazku

20 April 2015

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

5

Strana od-do

69-73

Kód UT WoS článku

000350186100010

EID výsledku v databázi Scopus

—